Vipel® F007-AAA-00 AOC Vinyl Ester

Product Description

Vipel Corrosion Resistant, Low VOC, Bisphenol A, Epoxy Vinyl Ester Resin

AOC's Vipel F007 is a low VOC, bisphenol A epoxy-based vinyl ester resin dissolved in styrene.

Versatile
The Vipel F007 Series is ideally suited for use in hand lay-up, spray-up, filament winding and pultrusion processes where outstanding mechanical properties and excellent resistance to chemicals and heat are required. Wide formulating capabilities allow for use in many processes and for optimization of cost/performance.

Corrosion resistance
Refer to AOC's "Corrosion Resistant Resin Guide under product F007" for corrosion resistance information. For questions regarding suitability of a resin to any particular chemical environment, contact AOC.

Food and Drug
All resins in this datasheet are manufactured from raw materials that are listed in FDA regulation Title 21 CFR 177.2420. It is the fabricator's responsibility to also be sure that the final composite is well cured. All composites used for FDA applications should be post cured at 180°F/82°C for at least 4 hours. After post curing, laminate should be washed with soap and water and rinsed.

General

Material Status

Commercial: Active

Availability

Africa & Middle East

Asia Pacific

Europe

Latin America

North America

South America

Features

Food Contact Acceptable

Good Corrosion Resistance

Uses

Coating Applications

Filaments

Agency Ratings

Forms

Liquid

Processing Method

Filament Winding

Hand Lay-up

Pultrusion

Spraying

Physical	Nominal Value	Unit	Test Method
Specific Gravity
Styrene Content		%
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus		psi	ASTM D638
Tensile Strength (Yield)		psi	ASTM D638
Tensile Elongation (Break)		%	ASTM D638
Flexural Modulus		psi	ASTM D790
Flexural Strength		psi	ASTM D790
Hardness	Nominal Value	Unit	Test Method
Barcol Hardness			ASTM D2583
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (264 psi, Unannealed)		°F	ASTM D648
Thermoset	Nominal Value	Unit	Test Method
Thermoset Mix Viscosity² (77°F)		cP
Post Cure Time (180°F)		hr
Exotherm
Gel to Peak		min
Peak		°F
Gel Time³ (77°F)		min
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Vipel® F007-AAA-00, Vipel F007AAA00, Vipel® , Vipel, VipelF007AAA00, F 007, F 007 AAA 00, F007-AAA-00, F007AAA00, F007:AAA:00, F007/AAA/00, F007+AAA+00, F007_AAA_00, F007 AAA 00, F007, 007AAA, AAA00, Vinyl Ester, Epoxy, AOC, VinylEster, 007F
Features
Features may also be described by the following terms: Good Corrosion Resistance, Corrosion Resistant.
Agency Ratings
This plastic material has 1 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): FDA (1).

Notes

¹Typical properties: these are not to be construed as specifications.

²Brookfield RV viscosity spindle 2 at 20 rpm

³Gel time with 0.2% Cobalt 6%, 0.05% DMA and 1.25% MEKP

Vipel® F007-AAA-00

Vinyl Ester

Supplied by AOC, L.L.C.