Vipel® F701-FBY-45 AOC Polyester Alloy

Product Description

Vipel Corrosion Resistant Isophthalic Polyester Resin

AOC's Vipel F701 series resins are high molecular weight, two stage isophthalic, unsaturated polyester resin with the wet out, cure and handling characteristics of general purpose resins.
They have an excellent shelf life and are ideal for filament winding and spray-up. A few selected resins are listed below including the high viscosity base resin,Vipel F701-FHG-00.

Corrosion resistance
AOC's Vipel F701 series resins provides excellent corrosion resistance when used in contact with inorganic and organic acids. Solvent resistance is field-proven for many petroleum
products such as kerosene, heating oil and crude oils. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC.

Versatile
Suitable for various fabricating methods such as hand lay-up, spray-up, filament winding, etc.

Food and Drug
All resins in this datasheet are manufactured from raw materials that are listed in FDA regulation Title 21 CFR 177.2420. It is the fabricator's responsibility to also be sure that the final composite is well cured. All composites used for FDA applications should be post cured at 180°F/82°C for at least 4 hours. After post curing it should be washed with soap and water and rinsed.

General

Material Status

Commercial: Active

Availability

Africa & Middle East

Asia Pacific

Europe

Latin America

North America

South America

Features

Acid Resistant

Food Contact Acceptable

Good Corrosion Resistance

High Molecular Weight

Isophthalic

Solvent Resistant

Uses

Coating Applications

Filaments

Agency Ratings

Forms

Liquid

Processing Method

Filament Winding

Hand Lay-up

Spraying

Physical	Nominal Value	Unit	Test Method
Specific Gravity
Styrene Content		%
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus		psi	ASTM D638
Tensile Strength (Yield)		psi	ASTM D638
Tensile Elongation (Break)		%	ASTM D638
Flexural Modulus		psi	ASTM D790
Flexural Strength		psi	ASTM D790
Hardness	Nominal Value	Unit	Test Method
Barcol Hardness			ASTM D2583
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (264 psi, Unannealed)		°F	ASTM D648
Thermoset	Nominal Value	Unit	Test Method
Thermoset Mix Viscosity² (77°F)		cP
Post Cure Time (180°F)		hr
Exotherm
Gel to Peak		min
Peak		°F
Gel Time³ (77°F)		min
Additional Information	Nominal Value	Unit	Test Method
Thixotropic Index⁴
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Vipel® F701-FBY-45, Vipel F701FBY45, Vipel® , Vipel, VipelF701FBY45, F 701, F 701 FBY 45, F701-FBY-45, F701FBY45, F701:FBY:45, F701/FBY/45, F701+FBY+45, F701_FBY_45, F701 FBY 45, F701, 701FBY, FBY45, Polyester Alloy, Polyester, AOC, PolyesterAlloy, 701F
Features
Features may also be described by the following terms: Good Corrosion Resistance, Corrosion Resistant, High Molecular Weight, High MW.
Agency Ratings
This plastic material has 1 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): FDA (1).

Notes

¹Typical properties: these are not to be construed as specifications.

²Brookfield LV viscosity spindle 3 at 60 rpm

³Gel time with 1.25% MEKP

⁴2/20 rpm Thix Index

Vipel® F701-FBY-45

Polyester Alloy

Supplied by AOC, L.L.C.