Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (250°C/1.2 kg)
|
|
g/10 min
|
ASTM D1238 |
|
Melt Volume-Flow Rate (MVR) (250°C/1.2 kg)
|
|
in³/10min
|
ISO 1133 |
|
Molding Shrinkage
|
|
|
Internal Method |
|
Flow 2
|
|
in/in
|
|
|
Flow: 0.126 in
|
|
in/in
|
|
|
Across Flow 2
|
|
in/in
|
|
|
Water Absorption
|
|
|
ISO 62 |
|
Saturation, 73°F
|
|
%
|
|
|
Equilibrium, 73°F, 50% RH
|
|
%
|
|
|
Tensile Modulus
|
|
|
|
|
-- 3
|
|
psi
|
ASTM D638 |
|
--
|
|
psi
|
ISO 527-2/1 |
|
Tensile Strength
|
|
|
|
|
Yield 4
|
|
psi
|
ASTM D638 |
|
Yield
|
|
psi
|
ISO 527-2/5 |
|
Break 4
|
|
psi
|
ASTM D638 |
|
Break
|
|
psi
|
ISO 527-2/5 |
|
Tensile Elongation
|
|
|
|
|
Yield 4
|
|
%
|
ASTM D638 |
|
Yield
|
|
%
|
ISO 527-2/5 |
|
Break 4
|
|
%
|
ASTM D638 |
|
Break
|
|
%
|
ISO 527-2/5 |
|
Flexural Modulus
|
|
|
|
|
1.97 in Span 5
|
|
psi
|
ASTM D790 |
|
-- 6
|
|
psi
|
ISO 178 |
|
Flexural Strength
|
|
|
|
|
-- 6, 7
|
|
psi
|
ISO 178 |
|
Yield, 1.97 in Span 5
|
|
psi
|
ASTM D790 |
|
Charpy Notched Impact Strength 8
|
|
|
ISO 179/1eA |
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Charpy Unnotched Impact Strength 8
|
|
|
ISO 179/1eU |
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Notched Izod Impact
|
|
|
|
|
-22°F
|
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
|
ft·lb/in
|
ASTM D256 |
|
-22°F 9
|
|
ft·lb/in²
|
ISO 180/1A |
|
73°F 9
|
|
ft·lb/in²
|
ISO 180/1A |
|
Unnotched Izod Impact Strength 9
|
|
|
ISO 180/1U |
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Instrumented Dart Impact (73°F, Total Energy)
|
|
in·lb
|
ASTM D3763 |
|
Ball Indentation Hardness (H 358/30)
|
|
psi
|
ISO 2039-1 |
|
Heat Deflection Temperature
|
|
|
|
|
66 psi, Unannealed, 3.94 in Span 10
|
|
°F
|
ISO 75-2/Be |
|
264 psi, Unannealed, 0.126 in
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed, 3.94 in Span 10
|
|
°F
|
ISO 75-2/Ae |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ASTM D1525 11, ISO 306/B50 11 |
|
--
|
|
°F
|
ISO 306/B120 |
|
Ball Pressure Test (257°F)
|
|
|
IEC 60695-10-2 |
|
CLTE
|
|
|
|
|
Flow: -40 to 104°F
|
|
in/in/°F
|
ASTM E831 |
|
Flow: 73 to 176°F
|
|
in/in/°F
|
ISO 11359-2 |
|
Transverse: -40 to 104°F
|
|
in/in/°F
|
ASTM E831 |
|
Transverse: 73 to 176°F
|
|
in/in/°F
|
ISO 11359-2 |
|
Transverse: 73 to 302°F
|
|
in/in/°F
|
ISO 11359-2 |
|
Surface Resistivity
|
|
ohms
|
IEC 60093 |
|
Volume Resistivity
|
|
ohm·cm
|
IEC 60093 |
|
Relative Permittivity
|
|
|
IEC 60250 |
|
50 Hz
|
|
|
|
|
60 Hz
|
|
|
|
|
1 MHz
|
|
|
|
|
Dissipation Factor
|
|
|
IEC 60250 |
|
50 Hz
|
|
|
|
|
60 Hz
|
|
|
|
|
1 MHz
|
|
|
|
|
Comparative Tracking Index
|
|
|
IEC 60112 |
|
--
|
|
V
|
|
|
Solution B
|
|
V
|
|
|
Electric Strength
|
|
|
IEC 60243-1 |
|
0.0315 in, in Oil
|
|
V/mil
|
|
|
0.0630 in, in Oil
|
|
V/mil
|
|
|
0.126 in, in Oil
|
|
V/mil
|
|
|
Flame Rating - UL (0.0630 in, Testing by SABIC)
|
|
|
UL 94 |
|
Glow Wire Flammability Index (0.0394 in)
|
|
°F
|
IEC 60695-2-12 |
|
This supplier and product may also be known by these terms: GE Plastics, LNP Engineering Plastics, GE Polymerland
Product names can be difficult to match. You may have searched any one of these terms to find this product: VALOX* 4012G Resin, VALOX 4012G Resin, VALOX* , VALOX, VALOX4012GResin, 4012 G Resin, 4012G Resin, 4012G, GResin, 4012GResin, Polybutylene Terephthalate, PBT, Polyester, SABIC IP, PolybutyleneTerephthalate, G4012
|
|
Features may also be described by the following terms: Fast Cycle, Rapid Cycle, Productivity, Fast Molding Cycle.
|