Dynaflex™ G2701C

Dynaflex™ G2701C can be recycled as a filler or impact modifier for polyolefins, or can be recycled by grinding and reintroduction to the molding process. Similar to PP or PE recycling process, if separated appropriately, it can be recycled many times.

Municipality waste stream recycle code is "7" which is designated for "Other".

Please contact GLS Thermoplastic Elastomers for a copy of our Recyclability Compliance letter.

Product names can be difficult to match. You may have searched any one of these terms to find this product: Dynaflex™ G2701C, Dynaflex G2701C, Dynaflex™ , Dynaflex, DynaflexG2701C, G 2701 C, G2701C, G2701, 2701C, Thermoplastic Elastomer, TPE, GLS, ThermoplasticElastomer, 2701G

Features may also be described by the following terms: Good Colorability, Good Processability, Easy Processing, Good Stability.

Uses may also be described by the following terms: Transparent Parts, Translucent Parts, Transparent or Translucent Parts.

This plastic material has 1 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): FDA (1).

Color concentrates with polypropylene (PP), ethylene vinyl acetate (EVA), or low density polyethylene (LDPE) carriers are most suitable for coloring Dynaflex™ G2701C. Improved color dispension can be achieved by using higher melt flow concentrates (with a melt flow from 25 - 40 g/10 min). Typical loadings for color concentrates are 1% to 5% by weight. Liquid color can be used, but mineral oil based carriers may have a significant effect on the final hardness value. Concentrates based on PVC should not be used. A high color match consistency can be obtained by using precolored compounds available from GLS. The final determination of color concentrate suitability should be determined by customer trials.

Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).

Regrind levels up to 20% can be used with Dynaflex™ G2701C with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer.

Dynaflex™ G2701C has excellent melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer.

Drying is not Required

Injection Speed: 1 to 5 in/sec
1st Stage - Boost Pressure: 350 to 650 psi
2nd Stage - Hold Pressure: 50% of Boost
Hold Time (Thick Part): 4 to 10 sec
Hold Time (Thin Part): 1 to 3 sec