Versalloy™ XL 9045-1

Versalloy™ XL 9045-1 can be recycled as a filler or impact modifier for polyolefins, or can be recycled by grinding and reintroduction to the molding process. Similar to PP or PE recycling process, if separated appropriately, it can be recycled many times.

Municipality waste stream recycle code is "7" which is designated for "Other".

Please contact GLS Thermoplastic Elastomers for a copy of our Recyclability Compliance letter.

Product names can be difficult to match. You may have searched any one of these terms to find this product: Versalloy™ XL 9045-1, Versalloy XL 90451, Versalloy™ , Versalloy, VersalloyXL90451, XL 9045, XL 9045-1, XL 90451, XL 9045:1, XL 9045/1, XL 9045+1, XL 9045_1, XL 9045 1, XL9045, 90451, XL90451, XL9045_1, Thermoplastic Elastomer, TPE, GLS, ThermoplasticElastomer, 9045XL

Features may also be described by the following terms: Good Surface Finish, Good Colorability, Good Flow.

Uses may also be described by the following terms: Thin-walled Parts, Thin Walled Parts, Thin-wall Parts, Thin wall Parts, Thinwall Parts.

This plastic material has 1 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): FDA (1).

Color concentrates with polypropylene (PP) carrier are most suitable for coloring Versalloy™ XL 9045-1. Improved color dispersion can be achieved by using higher melt flow concentrates (with a melt flow from 25 - 40 g/10 min). Typical loadings for color concentrates are 1% to 5% by weight. Concentrates based on PVC should not be used. A high color match consistency can be obtained by the use of precolored compounds available from GLS. The final determination of color concentrate suitability should be determined by customer trials.

Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).

Regrind levels up to 20% can be used with Versalloy™ XL 9045-1 with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer.

Versalloy™ XL 9045-1 has good melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer.

Drying is not Required

Injection Speed: 1 to 5 in/sec
1st Stage - Boost Pressure: 300 to 700 psi
2nd Stage - Hold Pressure: 70% of Boost
Hold Time (Thick Part): 4 to 10 sec
Hold Time (Thin Part): 1 to 3 sec