Quattor EVA UE-1203F

Ethylene Vinyl Acetate Copolymer

Supplied by Quattor Petroquímica

The technical datasheet with complete property values for Quattor EVA UE-1203F is available to members of the Prospector Plastics Database.
Register to view full datasheet.
Register to View Full Datasheet
Product Description
Ethylene Vinyl Acetate Copolymer produced under high pressure conditions in an autoclave reactor. This resin contains low levels of vinyl acetate. It offers excellent transparency, good compatibility with other thermoplastics, and high mechanical strength at low temperatures.

This resin is recommended for extrusion of agricultural films, co-extruded films for foods packaging. In addition to that it can be blended with polyethylene for special applications.
General  
Material Status 
  • Commercial: Active
Availability 
  • North America
  • South America
  
Features 
  • Food Contact Acceptable
  • High Clarity
  • Low Temperature Strength
Uses 
  • Agricultural Applications
  • Blending
  • Film
  • Food Packaging
  
Agency Ratings 
 
Processing Method 
  • Film Extrusion
Physical
Nominal Value
Unit
Test Method
Density
g/cm³
 ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
g/10 min
 ASTM D1238
Vinyl Acetate Content
wt%
  
Mechanical
Nominal Value
Unit
Test Method
Tensile Strength (Break)
psi
 ASTM D638
Tensile Elongation (Break)
%
 ASTM D638
Films
Nominal Value
Unit
Test Method
Film Thickness - Tested
mil
  
Secant Modulus
     ASTM D882
1% Secant, MD: 1.5 mil, Blown Film
psi
  
1% Secant, TD: 1.5 mil, Blown Film
psi
  
Tensile Strength
     ASTM D882
MD: Break, 1.5 mil, Blown Film
psi
  
TD: Break, 1.5 mil, Blown Film
psi
  
Tensile Elongation
     ASTM D882
MD: Break, 1.5 mil, Blown Film
%
  
TD: Break, 1.5 mil, Blown Film
%
  
Dart Drop Impact (1.5 mil, Blown Film)
g
 ASTM D1709
Elmendorf Tear Strength
     ASTM D1922
MD: 1.5 mil, Blown Film
g
  
TD: 1.5 mil, Blown Film
g
  
Hardness
Nominal Value
Unit
Test Method
Durometer Hardness
     ASTM D2240
Shore A
 
  
Shore D
 
  
Thermal
Nominal Value
Unit
Test Method
Vicat Softening Temperature
°F
 ASTM D1525 2
Melting Temperature
°F
 ASTM D3418
Additional Information
Film data obtained on 38 µm thickness film produced on a 70 mm extruder, blow up ratio 2.2:1, die gap 1.2 mm

Specimen: According to ASTM-D 4703, annex 1 procedure C
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Quattor EVA UE-1203F, Quattor EVA UE1203F, Quattor EVA , QuattorEVAUE1203F, QuattorEVA, EVAUE 1203 F, UE, EVAUE-1203F, EVAUE1203F, EVAUE:1203F, EVAUE/1203F, EVAUE+1203F, EVAUE_1203F, EVAUE 1203F, EVAUE1203, EVAUE, UE 1203 F, UE-1203F, UE1203F, UE:1203F, UE/1203F, UE+1203F, UE_1203F, UE 1203F, UE1203, 1203F, Ethylene Vinyl Acetate Copolymer, EVA, Polyethylene, PE, Quattor Petroquimica, EthyleneVinylAcetateCopolymer, 1203UE, 1203EVAUE
Features
Features may also be described by the following terms: Low Temperature Strength, High Clarity.
Uses
Uses may also be described by the following terms: Food Packaging.
Agency Ratings
This plastic material has 2 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): ANVISA (1), USP (1).
Notes
1Typical properties: these are not to be construed as specifications.
2Rate B (120°C/h), Loading 1 (10 N)
 
IDES
Copyright © 2012 IDES
The information presented on this datasheet was acquired by IDES from the producer of the material. IDES makes substantial efforts to assure the accuracy of this data. However, IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.