Density
|
|
g/cm³
|
ASTM D1505 |
|
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
|
|
g/10 min
|
ASTM D1238 |
|
Coefficient of Friction (vs. Itself - Dynamic, Blown Film)
|
|
|
ASTM D1894 |
|
Film Thickness - Tested
|
|
mil
|
|
|
Tensile Strength
|
|
|
ASTM D882 |
|
MD: Yield, 0.98 mil, Blown Film
|
|
psi
|
|
|
TD: Yield, 0.98 mil, Blown Film
|
|
psi
|
|
|
MD: Break, 0.98 mil, Blown Film
|
|
psi
|
|
|
TD: Break, 0.98 mil, Blown Film
|
|
psi
|
|
|
Tensile Elongation
|
|
|
ASTM D882 |
|
MD: Yield, 0.98 mil, Blown Film
|
|
%
|
|
|
TD: Yield, 0.98 mil, Blown Film
|
|
%
|
|
|
MD: Break, 0.98 mil, Blown Film
|
|
%
|
|
|
TD: Break, 0.98 mil, Blown Film
|
|
%
|
|
|
Dart Drop Impact (0.98 mil, Blown Film)
|
|
g
|
ASTM D1709A |
|
Elmendorf Tear Strength
|
|
|
ASTM D1922 |
|
MD: 0.98 mil, Blown Film
|
|
g
|
|
|
TD: 0.98 mil, Blown Film
|
|
g
|
|
|
Vicat Softening Temperature
|
|
°F
|
ASTM D1525 |
|
Gloss (45°)
|
|
|
ASTM D2457 |
|
Haze
|
|
%
|
ASTM D1003 |
|
Film data obtained on 25 µm thickness film produced on a 70 mm extruder, blow up ratio 2.2:1, die gap 1.8 mm, and 120 kg/h output
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Quattor® BF-22010, Quattor BF22010, Quattor® , Quattor, QuattorBF22010, BF, BF-22010, BF22010, BF:22010, BF/22010, BF+22010, BF_22010, BF 22010, Polyethylene, Linear Low Density, Polyethylene Linear Low Density, LLDPE, Polyethylene, PE, Quattor Petroquimica, PolyethyleneLinearLowDensity, 22010BF
|
|
Features may also be described by the following terms: Butene Comonomer, Good Heat Seal.
|
|