Quattor PE UB-615C

Low Density Polyethylene

Supplied by Quattor Petroquímica

The technical datasheet with complete property values for Quattor PE UB-615C is available to members of the Prospector Plastics Database.
Register to view full datasheet.
Register to View Full Datasheet
Product Description
High molecular weight Low Density Polyethylene produced under high pressure conditions in a tubular reactor. It offers excellent processability and outstanding physical properties. Contains slip additive.

Typical blown film application includes high resistance shrink film and film for automatic packing.
General  
Material Status 
  • Commercial: Active
Availability 
  • North America
  • South America
  
Additive 
  • Slip
Features 
  • Food Contact Acceptable
  • Good Processability
  • High Molecular Weight
  • Slip
  
Uses 
  • Film
  • Packaging
  • Shrink Wrap
Agency Ratings 
Processing Method 
  • Blown Film
Physical
Nominal Value
Unit
Test Method
Density
g/cm³
 ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
g/10 min
 ASTM D1238
Mechanical
Nominal Value
Unit
Test Method
Tensile Strength (Break)
psi
 ASTM D638
Tensile Elongation (Break)
%
 ASTM D638
Coefficient of Friction (vs. Itself - Dynamic, Blown Film)
 
 ASTM D1894
Films
Nominal Value
Unit
Test Method
Film Thickness - Tested
mil
  
Secant Modulus
     ASTM D882
1% Secant, MD: 1.5 mil, Blown Film
psi
  
1% Secant, TD: 1.5 mil, Blown Film
psi
  
Tensile Strength
     ASTM D882
MD: Break, 1.5 mil, Blown Film
psi
  
TD: Break, 1.5 mil, Blown Film
psi
  
Tensile Elongation
     ASTM D882
MD: Break, 1.5 mil, Blown Film
%
  
TD: Break, 1.5 mil, Blown Film
%
  
Dart Drop Impact (1.5 mil, Blown Film)
g
 ASTM D1709
Elmendorf Tear Strength
     ASTM D1922
MD: 1.5 mil, Blown Film
g
  
TD: 1.5 mil, Blown Film
g
  
Thermal
Nominal Value
Unit
Test Method
Vicat Softening Temperature
°F
 ASTM D1525 2
Melting Temperature
°F
 ASTM D3418
Optical
Nominal Value
Unit
Test Method
Haze
%
 ASTM D1003
Additional Information
Film data obtained on 38 µm thickness film produced on a 70 mm extruder, blow up ratio 2.2:1, die gap 1.2 mm
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Quattor PE UB-615C, Quattor PE UB615C, Quattor PE , QuattorPEUB615C, QuattorPE, PEUB 615 C, UB, PEUB-615C, PEUB615C, PEUB:615C, PEUB/615C, PEUB+615C, PEUB_615C, PEUB 615C, PEUB615, PEUB, UB 615 C, UB-615C, UB615C, UB:615C, UB/615C, UB+615C, UB_615C, UB 615C, UB615, 615C, Polyethylene, Low Density, Polyethylene Low Density, LDPE, Polyethylene, PE, Quattor Petroquimica, PolyethyleneLowDensity, 615UB, 615PEUB
Features
Features may also be described by the following terms: High Molecular Weight, High MW, Good Processability, Easy Processing, Slip, Unspecified Slip.
Uses
Uses may also be described by the following terms: Shrink Wrap.
Agency Ratings
This plastic material has 1 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): ANVISA (1).
Extrusion
Nominal Value
Unit
 
Cylinder Zone 1 Temp.
°F
  
Cylinder Zone 2 Temp.
°F
  
Cylinder Zone 3 Temp.
°F
  
Cylinder Zone 4 Temp.
°F
  
Cylinder Zone 5 Temp.
°F
  
Extrusion Notes
Minimum Thickness: 40 microns single layer
Blow-up Ratio: 2.0 to 4.5:1
Notes
1Typical properties: these are not to be construed as specifications.
2Rate B (120°C/h), Loading 1 (10 N)
 
IDES
Copyright © 2012 IDES
The information presented on this datasheet was acquired by IDES from the producer of the material. IDES makes substantial efforts to assure the accuracy of this data. However, IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.