VICTREX HT 22CA30 Victrex Polyether Ketone (Carbon Fiber Reinforcement, 30%)

Product Description

High performance thermoplastic material, 30% carbon fibre reinforced PolyEtherKetone (PEK), semi crystalline, granules for injection moulding, standard flow, colour black.

Higher temperature applications for higher strength and stiffness in a static or dynamic system. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.

General

Material Status

Commercial: Active

Availability

Asia Pacific

Europe

North America

Filler / Reinforcement

Carbon Fiber Reinforcement, 30% Filler by Weight

Features

Food Contact Acceptable

Good Chemical Resistance

Good Flow

Good Wear Resistance

High Stiffness

High Strength

Low Friction

Semi Crystalline

Uses

High Temperature Applications

Appearance

Black

Forms

Granules

Processing Method

Injection Molding

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ISO 1183
Molding Shrinkage²			ISO 294-4
Across Flow: 392°F		%
Flow: 392°F		%
Water Absorption			ISO 62
73°F, 24 hr, 0.126 in		%
Equilibrium, 73°F, 0.126 in, 50% RH		%
Spiral Flow² (392°F, 39.4 mil)		in	Internal Method
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (73°F)		psi	ISO 527-2
Tensile Stress			ISO 527-2
Break, 73°F		psi
Break, 257°F		psi
Break, 347°F		psi
Break, 437°F		psi
Break, 527°F		psi
Tensile Strain (Break, 73°F)		%	ISO 527-2
Flexural Modulus (73°F)		psi	ISO 178
Flexural Strength			ISO 178
527°F		psi
347°F		psi
257°F		psi
73°F		psi
Compressive Stress			ISO 604
73°F		psi
248°F		psi
392°F		psi
482°F		psi
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (73°F)		ft·lb/in²	ISO 179/1eA
Charpy Unnotched Impact Strength (73°F)		ft·lb/in²	ISO 179/1U
Notched Izod Impact Strength (73°F)		ft·lb/in²	ISO 180/A
Unnotched Izod Impact Strength (73°F)		ft·lb/in²	ISO 180
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (264 psi, Unannealed)		°F	ISO 75-2/A
Glass Transition Temperature		°F	ISO 11357-2
Melting Temperature		°F	ISO 11357-3
CLTE			ISO 11359-2
Flow: > 306°F		in/in/°F
Flow: < 306°F		in/in/°F
Transverse: < 306°F		in/in/°F
Transverse: > 306°F		in/in/°F
Thermal Conductivity (73°F)		Btu·in/hr/ft²/°F	Internal Method
Specific Heat Capacity (73°F)		Btu/lb/°F	DSC
Electrical	Nominal Value	Unit	Test Method
Volume Resistivity³ (73°F)		ohm·cm	ASTM D4496
Flammability	Nominal Value	Unit	Test Method
Glow Wire Flammability Index (0.0787 in)		°F	IEC 60695-2-12
Toxicity			NES 713
CO content
CO2 content
Total gases
Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity (752°F)		Pa·s	ISO 11443
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: VICTREX® HT™ 22CA30, VICTREX HT 22CA30, VICTREX® HT™ , VICTREX HT, VICTREXHT22CA30, VICTREXHT, 22 CA 30, 22CA30, 22CA, CA30, Polyether Ketone, PEK, Polyaryletherketone, PAEK, Victrex, PolyetherKetone, CA22
Features
Features may also be described by the following terms: Semi-Crystalline, Good Flow, High Stiffness, High Strength, Good Wear Resistance, Wear Resistant, Good Chemical Resistance, Chemical Resistant, Low Friction.

Injection	Nominal Value	Unit
Drying Temperature		°F
Drying Time		hr
Hopper Temperature		°F
Rear Temperature		°F
Middle Temperature		°F
Front Temperature		°F
Nozzle Temperature		°F
Mold Temperature		°F
Injection Notes
Runner: Die / nozzle >3mm, manifold >3.5mm Gate: >2mm or 0.5 x part thickness

Notes

¹Typical properties: these are not to be construed as specifications.

²405°C nozzle

³1V

VICTREX® HT™ 22CA30

Polyether Ketone

Carbon Fiber Reinforcement, 30%