Bio-Flex F 1110 FKuR Biodegradable Polymers

Product Description

Bio-Flex® F 1110 (prev. Bio-Flex® 221 F)
Biodegradable compound for film extrusion

Compostable Compound according to EN 13 432, max. layer thickness 110µm
Certified according to: DIN Certco
Compound registration no.: 7W0087

General

Material Status

Commercial: Active

Availability

Europe

Features

Biodegradable

Compostable

Renewable Resource Content

Uses

Film

Agency Ratings

Forms

Pellets

Processing Method

Film Extrusion

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ISO 1183
Apparent Density		g/cm³	ISO 60
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)		g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg)		in³/10min	ISO 1133
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus		psi	ISO 527-2
Tensile Stress (Yield)		psi	ISO 527-2
Tensile Strain (Yield)		%	ISO 527-2
Flexural Modulus		psi	ISO 178
Elongation at Break
--			ISO 178
--			ISO 527
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature		°F	ISO 306/A
Melting Temperature (DSC)		°F	ISO 3146
Additional Information	Nominal Value	Unit	Test Method
Breaking Stress			ISO 527
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Bio-Flex® F 1110, BioFlex F 1110, Bio-Flex® , BioFlex, Bio:Flex®, Bio/Flex®, Bio+Flex®, Bio_Flex®, Bio Flex®, BioFlexF1110, Bio_Flex, Bio Flex, F 1110, F1110, Biodegradable Polymers, Biodeg Polymers, FKuR, BiodegradablePolymers, BiodegPolymers, 1110F
Features
Features may also be described by the following terms: Renewable Resources, From Renewable Resources, Renewable Resource Derived, Renewable Raw Materials, Renewable Resource Content.
Agency Ratings
This plastic material has 1 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): EN (1).

Extrusion	Nominal Value	Unit
Drying Temperature		°F
Drying Time		hr
Suggested Max Moisture		%
Cylinder Zone 1 Temp.		°F
Cylinder Zone 2 Temp.		°F
Cylinder Zone 3 Temp.		°F
Cylinder Zone 4 Temp.		°F
Adapter Temperature		°F
Melt Temperature		°F
Die Temperature		°F
Extrusion Notes
Water jacket (feed): 35 [°C] Die gap: 0.8 - 1.2 mm Die diameter: up to 400 mm Blow film ratio: 2.5 - 4

Notes

¹Typical properties: these are not to be construed as specifications.

Bio-Flex® F 1110

Biodegradable Polymers

Supplied by FKuR Kunststoff GmbH