Radici Compounds ABS200G20L

Acrylonitrile Butadiene Styrene

Glass Fiber Reinforcement, 20%

Supplied by Radici Plastics USA, Inc.

The technical datasheet with complete property values for Radici Compounds ABS200G20L is available to members of the Prospector Plastics Database.
Register to view full datasheet.
Register to View Full Datasheet
Product Description
One of the first commercial polymer alloy products, acrylonitrile butadiene styrene compounds can be tailored to meet the requirements of a very wide range of end-use application demands.

ABS200G20L is a compound based on a medium impact grade ABS formulation reinforced with 20% glass fiber, which substantially increases tensile strength and rigidity, especially at elevated temperatures. ABS200G20L is lubricated for ease of mold release.

Although ABS resins in general exhibit an unusually broad latitude in processing conditions, ABS200G20L should be molded at the higher end of the typical melt temperature range, at between 500-520°F, and with mold surface temperatures of between 120-160°F, to promote best flow and surface appearance.
General  
Material Status 
  • Commercial: Active
Availability 
  • North America
Filler / Reinforcement 
  • Glass Fiber Reinforcement, 20% Filler by Weight
Additive 
  • Lubricant
Features 
  • Good Mold Release
  • Lubricated
  
Physical
Nominal Value
Unit
Test Method
Specific Gravity
 
 ASTM D792
Molding Shrinkage - Flow (73°F, 0.125 in)
in/in
 ASTM D955
Water Absorption (73°F, 24 hr)
%
 ASTM D570
Mechanical
Nominal Value
Unit
Test Method
Tensile Strength (Break, 73°F)
psi
 ASTM D638
Tensile Elongation (Break, 73°F)
%
 ASTM D638
Flexural Modulus (73°F)
psi
 ASTM D790
Flexural Strength (73°F)
psi
 ASTM D790
Impact
Nominal Value
Unit
Test Method
Notched Izod Impact (73°F, 0.125 in)
ft·lb/in
 ASTM D256
Hardness
Nominal Value
Unit
Test Method
Rockwell Hardness (M-Scale, 73°F)
 
 ASTM D785
Thermal
Nominal Value
Unit
Test Method
Deflection Temperature Under Load (264 psi, Unannealed)
°F
 ASTM D648
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Radici Compounds ABS200G20L, Radici Compounds , RadiciCompoundsABS200G20L, RadiciCompounds, CompoundsABS 200 G 20 L, CompoundsABS200G20L, CompoundsABS200, Compounds, ABS 200 G 20 L, ABS200G20L, ABS200, 200G, G20, 20L, Acrylonitrile Butadiene Styrene, ABS, Radici USA, AcrylonitrileButadieneStyrene, 200ABS, 200CompoundsABS
Features
Features may also be described by the following terms: Good Mold Release, Easy Release, Good Demolding.
Injection
Nominal Value
Unit
 
Drying Temperature
°F
  
Drying Time
hr
  
Suggested Max Moisture
%
  
Rear Temperature
°F
  
Middle Temperature
°F
  
Front Temperature
°F
  
Processing (Melt) Temp
°F
  
Mold Temperature
°F
  
Back Pressure
psi
  
Screw Speed
rpm
  
Cushion
in
  
Notes
1Typical properties: these are not to be construed as specifications.
 
IDES
Copyright © 2012 IDES
The information presented on this datasheet was acquired by IDES from the producer of the material. IDES makes substantial efforts to assure the accuracy of this data. However, IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.