Arak LLDPE LL0209AA / LL0209KJ Arak Petrochemical Polyethylene, Linear Low Density

Product Description

LL0209AA & LL0209KJ are linear low density polyethylene copolymers containing butene-1 as a co-monomer.

LL0209AA & LL0209KJ are suitable for general purpose films, neat or in lean blends with LDPE and other ethylene polymers. Lean blends applications include sacks of all types, FFS and agricultural films.
In lean blends they offer the following advantages:

Greater draw down.

Improved hot-tack and lower seal shrinkage.

Better tear resistance.

Higher tensile stress and elongation at break.

LL0209KJ offers high slip film with easy opening properties when used pure in thickness range 35-100 microns. Addition of other polymers, master batches and pigments or use of other thickness may alter film slip and anti-block performance.

If corona treatment is necessary, the level should normally be in the range 38-48 mN/m.
LL0209AA & LL0209KJ should be stored in the dry condition below the 50°C and avoided from the exposure of direct sunlight.

Recommended melt temperature for extrusion is about 180°C - 225°C.

* LL0209AA & LL0209KJ are suitable for food contact.

General

Material Status

Commercial: Active

Availability

Africa & Middle East

Additive

High Slip

Features

Butene Comonomer

Copolymer

Food Contact Acceptable

Good Drawdown

Good Tear Strength

High Elongation

High Slip

High Tensile Strength

Hot Tack Strength

Uses

Blending

Film

General Purpose

Processing Method

Film Extrusion

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ASTM D2838
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)		g/10 min	ASTM D1238
Films	Nominal Value	Unit	Test Method
Film Thickness - Tested		mil
Film Thickness - Recommended / Available
Tensile Strength			ASTM D882
MD: Yield		psi
TD: Yield		psi
MD: Break		psi
TD: Break		psi
Tensile Elongation			ASTM D882
MD: Break		%
TD: Break		%
Dart Drop Impact		g	ASTM D1709
Elmendorf Tear Strength			ASTM D1922
MD: 0.98 mil		g
TD: 0.98 mil		g
Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature		°F	ASTM D1525
Optical	Nominal Value	Unit	Test Method
Gloss (45°)			ASTM D2457
Haze		%	ASTM D1003
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Arak LLDPE LL0209AA / LL0209KJ, Arak LLDPE LL0209AA LL0209KJ, Arak LLDPE , ArakLLDPELL0209AALL0209KJ, ArakLLDPE, LL 0209 AA, LLDPELL 0209 AA LL 0209 KJ, LLDPELL 0209 AA, LL0209AA, LLDPELL0209AA / LL0209KJ, LLDPELL0209AA LL0209KJ, LLDPELL0209AA : LL0209KJ, LLDPELL0209AA + LL0209KJ, LLDPELL0209AA - LL0209KJ, LLDPELL0209AA _ LL0209KJ, LLDPELL0209AA LL0209KJ, LLDPELL0209, LLDPELL0209AA, LL 0209 AA LL 0209 KJ, LLDPELL0209AALL0209KJ, LL0209AA / LL0209KJ, LL0209AA LL0209KJ, LL0209AA : LL0209KJ, LL0209AA + LL0209KJ, LL0209AA - LL0209KJ, LL0209AA _ LL0209KJ, LL0209AA LL0209KJ, LL0209, 0209AA, AALL, 0209KJ, LLDPELL0209AA_LL0209KJ, LL0209AALL0209KJ, LL0209AA_LL0209KJ, Polyethylene, Linear Low Density, Polyethylene Linear Low Density, LLDPE, Polyethylene, PE, Arak Petrochemical, PolyethyleneLinearLowDensity, 0209LL, 0209LLDPELL
Features
Features may also be described by the following terms: Butene Comonomer, Good Drawdown, Good draw down, Hot Tack Strength, High Elongation, Good Tear Strength, High Tensile Strength, High Slip.

Extrusion	Nominal Value	Unit
Drying Temperature		°F
Melt Temperature		°F

Notes

¹Typical properties: these are not to be construed as specifications.

Arak LLDPE LL0209AA / LL0209KJ

Linear Low Density Polyethylene

Supplied by Arak Petrochemical Corporation