Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (250°C/2.16 kg)
|
|
g/10 min
|
ASTM D1238, ISO 1133 |
|
Molding Shrinkage
|
|
|
ASTM D955 |
|
Flow
|
|
in/in
|
|
|
Across Flow
|
|
in/in
|
|
|
Water Absorption
|
|
|
|
|
73°F, 24 hr
|
|
%
|
ASTM D570, ISO 62 |
|
Saturation
|
|
%
|
ASTM D570 |
|
Saturation, 73°F
|
|
%
|
ISO 62 |
|
Tensile Modulus
|
|
psi
|
ASTM D638, ISO 527-2 |
|
Tensile Strength (Break)
|
|
psi
|
ASTM D638, ISO 527-2 |
|
Tensile Elongation (Break)
|
|
%
|
ASTM D638, ISO 527-2 |
|
Flexural Modulus
|
|
psi
|
ASTM D790, ISO 178 |
|
Flexural Strength
|
|
|
|
|
--
|
|
psi
|
ISO 178 |
|
Break
|
|
psi
|
ASTM D790 |
|
Charpy Notched Impact Strength 2 (73°F)
|
|
ft·lb/in²
|
ASTM D256, ISO 179 |
|
Notched Izod Impact (73°F, 0.126 in)
|
|
ft·lb/in
|
ISO 180, ASTM D256 |
|
Rockwell Hardness (R-Scale)
|
|
|
ASTM D785 |
|
Deflection Temperature Under Load (264 psi, Unannealed)
|
|
°F
|
ASTM D648, ISO 75-2/A |
|
Vicat Softening Temperature
|
|
°F
|
ISO 306/B50, ASTM D1525 3 |
|
Melting Temperature
|
|
°F
|
ASTM D211, ISO 121 |
|
Dielectric Strength (0.0787 in)
|
|
V/mil
|
ASTM D149 |
|
Comparative Tracking Index (Solution A)
|
|
V
|
IEC 60112 |
|
Flame Rating - UL (0.0630 in)
|
|
|
UL 94 |
|
Glow Wire Ignition Temperature (0.0787 in)
|
|
°F
|
IEC 60695-2-13 |
|
Oxygen Index
|
|
%
|
ASTM D2863 |
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: TAROLOX 200 G4, TAROLOX , TAROLOX200G4, 200 G 4, 200 G4, 200G, G4, 200G4, Polybutylene Terephthalate, PBT, Polyester, Taro Plast, PolybutyleneTerephthalate, G200
|
|
Features may also be described by the following terms: Good Flow, Good Surface Finish, Good Dimensional Stability, Dimensionally Stable, Heat Stabilized, Heat-ageing Stabilized, Heat Ageing Stabilized, Heat-aging Stabilized, Heat Aging Stabilized, Good Mold Release, Easy Release, Good Demolding, Low Warpage, Low Warp.
|