TAROLOX 111 G6 DX02 Taro Plast Polyethylene Terephthalate (Glass Fiber Reinforcement, 30%)

Product Description

PET glass fiber reinforced 30%, self extinguishing V0 without PBDE/PBDF, high temperature resistance, good flow, very good mechanical, thermal and electrical properties, low moisture absorption, good dimensional stability. Product must be dried before moulding.

UL94 V0 approved all colours at 1,5 mm - V2 at 0,75 mm. UL 746B under testing.

Available: all colors, heat stabilized (H), release agent (W).

General

Material Status

Commercial: Active

Availability

Europe

Filler / Reinforcement

Glass Fiber Reinforcement, 30% Filler by Weight

Additive

Heat Stabilizer

Mold Release

Features

Good Dimensional Stability

Good Electrical Properties

Good Flow

Good Mold Release

Heat Stabilized

High Heat Resistance

Low Moisture Absorption

Self Extinguishing

Appearance

Colors Available

Forms

Pellets

Processing Method

Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity
--			ASTM D792
--		g/cm³	ISO 1183
Molding Shrinkage			ASTM D955
Flow		in/in
Across Flow		in/in
Water Absorption (73°F, 24 hr)		%	ASTM D570, ISO 62
Granule Humidity		%	Internal Method
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus		psi	ASTM D638, ISO 527-2
Tensile Elongation (Break)		%	ASTM D638, ISO 527-2
Flexural Modulus		psi	ASTM D790, ISO 178
Flexural Strength
--		psi	ISO 178
Break		psi	ASTM D790
Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (73°F, 0.126 in)		ft·lb/in	ISO 180, ASTM D256
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (264 psi, Unannealed)		°F	ASTM D648, ISO 75-2/A
Vicat Softening Temperature		°F	ISO 306/B50, ASTM D1525²
Melting Temperature		°F	ASTM D211, ISO 121
Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)		V	IEC 60112
Flammability	Nominal Value	Unit	Test Method
Flame Rating - UL			UL 94
0.0295 in
0.0591 in
0.126 in
Glow Wire Ignition Temperature (0.0787 in)		°F	IEC 60695-2-13
Oxygen Index		%	ASTM D2863
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: TAROLOX 111 G6 DX02, TAROLOX , TAROLOX111G6DX02, 111 G 6 DX 02, 111 G6 DX02, 111G, G6, 6DX, DX02, 111G6DX02, Polyethylene Terephthalate, PET, Polyester, Taro Plast, PolyethyleneTerephthalate, G111
Features
Features may also be described by the following terms: Self Extinguishing, Self-Extinguishing, Good Electrical Properties, High Heat Resistance, Good Flow, Low Moisture Absorption, Low Water Absorption, Water Resistant, Moisture Resistant, Good Dimensional Stability, Dimensionally Stable, Heat Stabilized, Heat-ageing Stabilized, Heat Ageing Stabilized, Heat-aging Stabilized, Heat Aging Stabilized, Good Mold Release, Easy Release, Good Demolding.

Injection	Nominal Value	Unit
Drying Temperature		°F
Drying Time		hr
Processing (Melt) Temp		°F
Mold Temperature		°F
Injection Rate

Notes

¹Typical properties: these are not to be construed as specifications.

²Rate A (50°C/h), Loading 2 (50 N)

TAROLOX 111 G6 DX02

Polyethylene Terephthalate

Glass Fiber Reinforcement, 30%

Supplied by Taro Plast S.p.A.