Density
|
|
--
|
g/cm³
|
ISO 1183/A |
|
Tensile Modulus
|
|
|
psi
|
ISO 527-2/1A/1 |
|
Tensile Stress (Break)
|
|
|
psi
|
ISO 527-2/1A/5 |
|
Tensile Strain (Break)
|
|
|
%
|
ISO 527-2/1A/5 |
|
Flexural Modulus
|
|
--
|
psi
|
ISO 178 |
|
Flexural Strength
|
|
--
|
psi
|
ISO 178 |
|
Flexural Strain at Flexural Strength
|
|
--
|
%
|
ISO 178 |
|
Charpy Notched Impact Strength
|
|
|
|
ISO 179/1eA |
|
-22°F
|
|
--
|
ft·lb/in²
|
|
|
73°F
|
|
|
ft·lb/in²
|
|
|
Charpy Unnotched Impact Strength
|
|
|
|
ISO 179/1eU |
|
-22°F
|
|
--
|
ft·lb/in²
|
|
|
73°F
|
|
|
ft·lb/in²
|
|
|
Heat Deflection Temperature
|
|
|
|
|
|
66 psi, Unannealed
|
|
--
|
°F
|
ISO 75-2/Bf |
|
264 psi, Unannealed
|
|
--
|
°F
|
ISO 75-2/Af |
|
Vicat Softening Temperature
|
|
|
|
|
|
--
|
|
--
|
°F
|
ISO 306/A50 |
|
--
|
|
--
|
°F
|
ISO 306/B50 |
|
Burning Rate
|
|
--
|
in/min
|
ISO 3795 |
|
Flammability Classification
|
|
|
|
IEC 60695-11-10, -20 |
|
0.0591 in
|
|
--
|
|
|
|
0.118 in
|
|
--
|
|
|
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: SCHULAMID® 6 GF 30 TC, SCHULAMID 6 GF 30 TC, SCHULAMID® , SCHULAMID, SCHULAMID6GF30TC, 6 GF 30 TC, 6GF, GF30, 30TC, 6GF30TC, Polyamide 6, Nylon 6, Polyamide, Nylon, pa6, A. Schulman Eur, Polyamide6, Nylon6, GF6
|
|
|
Generic Name may also be described by the following terms: PA6.
|
|
|
Generic Name may also be described by the following terms: PA6.
|
|
|
Features may also be described by the following terms: Low Density, Low Specific Gravity, Good Dimensional Stability, Dimensionally Stable, Good Flow, Low Gloss, Low Moisture Absorption, Low Water Absorption, Water Resistant, Moisture Resistant, Good Processability, Easy Processing.
|
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: SCHULAMID® 6 GF 30 TC, SCHULAMID 6 GF 30 TC, SCHULAMID® , SCHULAMID, SCHULAMID6GF30TC, 6 GF 30 TC, 6GF, GF30, 30TC, 6GF30TC, Polyamide 6, Nylon 6, Polyamide, Nylon, pa6, A. Schulman Eur, Polyamide6, Nylon6, GF6
|