LNP* Lubricomp* DFL22

Polycarbonate

Glass Fiber Reinforcement

Supplied by SABIC Innovative Plastics Asia Pacific

The technical datasheet with complete property values for LNP* Lubricomp* DFL22 is available to members of the Prospector Plastics Database.
Register to view full datasheet.
Register to View Full Datasheet
Product Description
LNP* Lubricomp* DFL22 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.

Also known as: LNP* Lubricomp* Compound DFL-4022
Product reorder name: DFL22
General  
Material Status 
  • Commercial: Active
Availability 
  • Asia Pacific
Filler / Reinforcement 
  • Glass Fiber Reinforcement
Additive 
  • PTFE Lubricant
Features 
  • Lubricated
Processing Method 
  • Injection Molding
Physical
Nominal Value
Unit
Test Method
Specific Gravity
      
--
 
 ASTM D792
--
g/cm³
 ISO 1183
Molding Shrinkage
      
Flow: 24 hr
in/in
 ASTM D955
Across Flow: 24 hr
in/in
 ASTM D955
Across Flow: 24 hr
%
 ISO 294-4
Flow: 24 hr
%
 ISO 294-4
Water Absorption (24 hr, 50% RH)
%
 ASTM D570
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
      
-- 2
psi
 ASTM D638
--
psi
 ISO 527-2/1
Tensile Strength
      
Yield
psi
 ASTM D638
Yield 3
psi
 ASTM D638
Yield
psi
 ISO 527-2, ISO 527-2/5
Break
psi
 ASTM D638
Break 3
psi
 ASTM D638
Break
psi
 ISO 527-2, ISO 527-2/5
Tensile Elongation
      
Yield
%
 ASTM D638, ISO 527-2, ISO 527-2/5
Yield 3
%
 ASTM D638
Break
%
 ASTM D638
Break 3
%
 ASTM D638
Break
%
 ISO 527-2, ISO 527-2/5
Flexural Modulus
      
--
psi
 ASTM D790
1.97 in Span 4
psi
 ASTM D790
--
psi
 ISO 178
-- 5
psi
 ISO 178
Flexural Strength
     ISO 178
-- 5, 6
psi
  
--
psi
  
Coefficient of Friction
     ASTM D3702 Modified
vs. Itself - Dynamic
 
  
vs. Itself - Static
 
  
Wear Factor - Washer
10^-10 in^5-min/ft-lb-hr
 ASTM D3702 Modified
Impact
Nominal Value
Unit
Test Method
Notched Izod Impact
      
73°F
ft·lb/in
 ASTM D256
73°F 7
ft·lb/in²
 ISO 180/1A
Unnotched Izod Impact
      
73°F
ft·lb/in
 ASTM D4812
73°F 7
ft·lb/in²
 ISO 180/1U
Instrumented Dart Impact
      
73°F, Energy at Peak Load
in·lb
 ASTM D3763
--
ft·lb
 ISO 6603-2
Thermal
Nominal Value
Unit
Test Method
Deflection Temperature Under Load
      
66 psi, Unannealed, 0.126 in
°F
 ASTM D648
66 psi, Unannealed, 2.52 in Span 8
°F
 ISO 75-2/Bf
264 psi, Unannealed, 0.126 in
°F
 ASTM D648
264 psi, Unannealed, 2.52 in Span 8
°F
 ISO 75-2/Af
CLTE
      
Flow: -40 to 104°F
in/in/°F
 ASTM E831, ISO 11359-2
Flow: 73 to 140°F
in/in/°F
 ISO 11359-2
Transverse: -40 to 104°F
in/in/°F
 ASTM E831, ISO 11359-2
Transverse: 73 to 140°F
in/in/°F
 ISO 11359-2
Related Terminology
This supplier and product may also be known by these terms: GE Plastics, LNP Engineering Plastics

Product names can be difficult to match. You may have searched any one of these terms to find this product: LNP* Lubricomp* DFL22, LNP Lubricomp DFL22, LNP* Lubricomp* , LNP Lubricomp, LNPLubricompDFL22, LNPLubricomp, DFL 22, DFL22, Polycarbonate, PC, SABIC IP Asia, 22DFL
Injection
Nominal Value
Unit
 
Drying Temperature
°F
  
Drying Time
hr
  
Suggested Max Moisture
%
  
Rear Temperature
°F
  
Middle Temperature
°F
  
Front Temperature
°F
  
Processing (Melt) Temp
°F
  
Mold Temperature
°F
  
Back Pressure
psi
  
Screw Speed
rpm
  
Notes
1Typical properties: these are not to be construed as specifications.
22.0 in/min
3Type I, 0.20 in/min
40.051 in/min
50.079 in/min
6Yield
780*10*4
880*10*4 mm
 
IDES
Copyright © 2012 IDES
The information presented on this datasheet was acquired by IDES from the producer of the material. IDES makes substantial efforts to assure the accuracy of this data. However, IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.