Density
|
|
g/cm³
|
ISO 1183 |
|
Apparent Density
|
|
g/cm³
|
ISO 60 |
|
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)
|
|
g/10 min
|
ISO 1133 |
|
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg)
|
|
in³/10min
|
ISO 1133 |
|
Molding Shrinkage
|
|
|
|
|
Across Flow
|
|
%
|
ISO 2577 |
|
Flow
|
|
%
|
ISO 2577 |
|
Across Flow: 0.0787 in 2
|
|
%
|
ISO 294-4 |
|
Flow: 0.0787 in 2
|
|
%
|
ISO 294-4 |
|
Water Absorption
|
|
|
ISO 62 |
|
Saturation, 73°F
|
|
%
|
|
|
Equilibrium, 73°F, 50% RH
|
|
%
|
|
|
Tensile Modulus (73°F)
|
|
psi
|
ISO 527-2/1 |
|
Tensile Stress
|
|
|
ISO 527-2/50 |
|
Yield, 73°F
|
|
psi
|
|
|
Break, 73°F
|
|
psi
|
|
|
Tensile Strain
|
|
|
ISO 527-2/50 |
|
Yield, 73°F
|
|
%
|
|
|
Break, 73°F
|
|
%
|
|
|
Nominal Tensile Strain at Break (73°F)
|
|
%
|
ISO 527-2/50 |
|
Flexural Modulus 3 (73°F)
|
|
psi
|
ISO 178 |
|
Flexural Strength 3
|
|
|
ISO 178 |
|
3.5% Strain, 73°F
|
|
psi
|
|
|
73°F
|
|
psi
|
|
|
Flexural Strain at Flexural Strength 4 (73°F)
|
|
%
|
ISO 178 |
|
Water Vapor Transmission Rate (73°F, 3.9 mil, 85% RH)
|
|
g/100 in²/24 hr
|
ISO 15106-1 |
|
Charpy Notched Impact Strength
|
|
|
ISO 179/1 e A |
|
-22°F, Complete Break 5
|
|
ft·lb/in²
|
|
|
73°F, Partial Break 6
|
|
ft·lb/in²
|
|
|
Charpy Unnotched Impact Strength
|
|
|
ISO 179/1 eU |
|
-22°F
|
|
|
|
|
73°F
|
|
|
|
|
Notched Izod Impact Strength 7
|
|
|
ISO 180/A |
|
-22°F, Complete Break
|
|
ft·lb/in²
|
|
|
73°F, Partial Break
|
|
ft·lb/in²
|
|
|
Multi-Axial Instrumented Impact Energy
|
|
|
ISO 6603-2 |
|
-22°F
|
|
ft·lb
|
|
|
73°F
|
|
ft·lb
|
|
|
Multi-Axial Instrumented Impact Peak Force
|
|
|
ISO 6603-2 |
|
-22°F
|
|
lbf
|
|
|
73°F
|
|
lbf
|
|
|
Heat Deflection Temperature
|
|
|
|
|
66 psi, Unannealed
|
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
|
°F
|
ISO 75-2/A |
|
Glass Transition Temperature 8
|
|
°F
|
ISO 11357-2 |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ISO 306/B50 |
|
--
|
|
°F
|
ISO 306/B120 |
|
Ball Pressure Test (277°F)
|
|
|
IEC 60695-10-2 |
|
CLTE
|
|
|
ISO 11359-2 |
|
Flow: 73 to 131°F
|
|
in/in/°F
|
|
|
Transverse: 73 to 131°F
|
|
in/in/°F
|
|
|
Thermal Conductivity (73°F)
|
|
Btu·in/hr/ft²/°F
|
ISO 8302 |
|
Surface Resistivity
|
|
ohm
|
IEC 60093 |
|
Volume Resistivity (73°F)
|
|
ohm·cm
|
IEC 60093 |
|
Relative Permittivity
|
|
|
IEC 60250 |
|
73°F, 100 Hz
|
|
|
|
|
73°F, 1 MHz
|
|
|
|
|
Dissipation Factor
|
|
|
IEC 60250 |
|
73°F, 100 Hz
|
|
|
|
|
73°F, 1 MHz
|
|
|
|
|
Comparative Tracking Index
|
|
|
IEC 60112 |
|
Solution A
|
|
V
|
|
|
Solution B
|
|
V
|
|
|
Electric Strength (0.0394 in)
|
|
V/mil
|
IEC 60243-1 |
|
Flame Rating - UL
|
|
|
UL 94 |
|
0.0591 in
|
|
|
|
|
0.118 in
|
|
|
|
|
Glow Wire Flammability Index
|
|
|
IEC 60695-2-12 |
|
0.0394 in
|
|
°F
|
|
|
0.0591 in
|
|
°F
|
|
|
0.0787 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
0.157 in
|
|
°F
|
|
|
Oxygen Index 9
|
|
%
|
ISO 4589-2 |
|
Burning Rate (> 39.4 mil)
|
|
|
ISO 3795 |
|
Flash Ignition Temperature
|
|
°F
|
ASTM D1929 |
|
Self Ingnition Temperature
|
|
°F
|
ASTM D1929 |
|
RTI Str (0.0591 in)
|
|
°F
|
UL 746 |
|
RTI Imp (0.0591 in)
|
|
°F
|
UL 746 |
|
RTI Elec (0.0591 in)
|
|
°F
|
UL 746 |
|
Refractive Index 10
|
|
|
ISO 489 |
|
Transmittance
|
|
|
ISO 13468-2 |
|
39.4 mil
|
|
%
|
|
|
78.7 mil
|
|
%
|
|
|
118 mil
|
|
%
|
|
|
157 mil
|
|
%
|
|
|
Electrolytical Corrosion
|
|
|
IEC 60426 |
|
ISO Shortname
|
|
|
ISO 7391 |
|
This supplier and product may also be known by these terms: Macrolon, Makralon
Product names can be difficult to match. You may have searched any one of these terms to find this product: Makrolon® 6455, Makrolon 6455, Makrolon® , Makrolon, Makrolon6455, 6455, Polycarbonate, PC, Bayer
|
|
Features may also be described by the following terms: No Chlorine Content, Chlorine Free, Bromine Free, No Bromine Content, Medium Viscosity, Good Mold Release, Easy Release, Good Demolding.
|
|
This plastic material has 3 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): EU (3).
|