Density
|
|
--
|
g/cm³
|
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (325°C/5.0 kg)
|
|
--
|
in³/10min
|
ISO 1133 |
|
Molding Shrinkage
|
|
--
|
%
|
ISO 294-4 |
|
Water Absorption
|
|
|
|
ISO 62 |
|
Saturation, 73°F
|
|
--
|
%
|
|
|
Equilibrium, 73°F, 50% RH
|
|
--
|
%
|
|
|
Viscosity Number (H2SO4 (Sulphuric Acid))
|
|
--
|
cm³/g
|
ISO 307 |
|
Tensile Modulus (73°F)
|
|
|
psi
|
ISO 527-2 |
|
Tensile Stress (Yield, 73°F)
|
|
|
psi
|
ISO 527-2/50 |
|
Tensile Strain (Yield, 73°F)
|
|
|
%
|
ISO 527-2/50 |
|
Nominal Tensile Strain at Break (73°F)
|
|
|
%
|
ISO 527-2/50 |
|
Tensile Creep Modulus (1000 hr)
|
--
|
|
psi
|
ISO 899-1 |
|
Flexural Modulus (73°F)
|
|
--
|
psi
|
ISO 178 |
|
Charpy Notched Impact Strength
|
|
|
|
ISO 179/1eA |
|
-22°F
|
|
--
|
ft·lb/in²
|
|
|
73°F
|
|
--
|
ft·lb/in²
|
|
|
Charpy Unnotched Impact Strength
|
|
|
|
ISO 179/1eU |
|
-22°F
|
|
--
|
ft·lb/in²
|
|
|
73°F
|
|
--
|
ft·lb/in²
|
|
|
Notched Izod Impact Strength (73°F)
|
|
--
|
ft·lb/in²
|
ISO 180/1A |
|
Heat Deflection Temperature (264 psi, Unannealed)
|
|
--
|
°F
|
ISO 75-2/A |
|
Melting Temperature (DSC)
|
|
--
|
°F
|
ISO 3146 |
|
CLTE - Flow (73 to 176°F)
|
|
--
|
in/in/°F
|
ISO 11359-2 |
|
Thermal Conductivity
|
|
--
|
Btu·in/hr/ft²/°F
|
ISO 8302 |
|
Volume Resistivity
|
|
|
ohm·cm
|
IEC 60093 |
|
Relative Permittivity (73°F, 1 MHz)
|
|
|
|
IEC 60250 |
|
Dissipation Factor (73°F, 1 MHz)
|
|
|
|
IEC 60250 |
|
Comparative Tracking Index (Solution A)
|
|
--
|
V
|
IEC 60112 |
|
Flame Rating - UL (0.0630 in)
|
|
--
|
|
UL 94 |
|
|
The value listed as Thermal Conductivity, ISO 8302, was tested in accordance with DIN 52612-2.
Maximum Service Temperature (Short Cycle Operation): 250°C
Moisture Absorption, Equilibrium, ISO 62, 23°C, 50% RH: 1.6 to 2%
Specific Heat Capacity: 1500 J/(kg K)
Temperature Index at 50% Loss of Tensile Strength after 20000h, IEC 216: 110°C
Temperature Index at 50% Loss of Tensile Strength after 5000h, IEC 216: 130°C
Water Absorption, Saturation in Water, ISO 62, 23°C: 6.5 to 7.5%
|
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Ultramid® T KR4350, Ultramid T KR4350, Ultramid® T , Ultramid T, UltramidTKR4350, UltramidT, TKR 4350, TKR4350, KR 4350, KR4350, Polyamide 6/6T Copolymer, Polyamide 66T Copolymer, Polyamide 6:6T Copolymer, Polyamide 6+6T Copolymer, Polyamide 6-6T Copolymer, Polyamide 6_6T Copolymer, Polyamide 6 6T Copolymer, Nylon 6/6T, Nylon 66T, Nylon 6:6T, Nylon 6+6T, Nylon 6-6T, Nylon 6_6T, Nylon 6 6T, Polyamide, Nylon, BASF, Polyamide66TCopolymer, Nylon66T, Polyamide6_6TCopolymer, Nylon6_6T, 4350KR, 4350TKR
|
|
|
Generic Name may also be described by the following terms: PA6/6T.
|
|
|
Generic Name may also be described by the following terms: PA6/6T.
|
|
|
Features may also be described by the following terms: Ultra High Toughness, High Strength, High Stiffness, Low Water Absorption, Low Moisture Absorption, Water Resistant, Moisure Resistant.
|
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Ultramid® T KR4350, Ultramid T KR4350, Ultramid® T , Ultramid T, UltramidTKR4350, UltramidT, TKR 4350, TKR4350, KR 4350, KR4350, Polyamide 6/6T Copolymer, Polyamide 66T Copolymer, Polyamide 6:6T Copolymer, Polyamide 6+6T Copolymer, Polyamide 6-6T Copolymer, Polyamide 6_6T Copolymer, Polyamide 6 6T Copolymer, Nylon 6/6T, Nylon 66T, Nylon 6:6T, Nylon 6+6T, Nylon 6-6T, Nylon 6_6T, Nylon 6 6T, Polyamide, Nylon, BASF, Polyamide66TCopolymer, Nylon66T, Polyamide6_6TCopolymer, Nylon6_6T, 4350KR, 4350TKR
|