Density
|
|
--
|
g/cm³
|
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (275°C/5.0 kg)
|
|
--
|
in³/10min
|
ISO 1133 |
|
Molding Shrinkage
|
|
--
|
%
|
ISO 294-4 |
|
Water Absorption
|
|
|
|
ISO 62 |
|
Saturation, 73°F
|
|
--
|
%
|
|
|
Equilibrium, 73°F, 50% RH
|
|
--
|
%
|
|
|
Viscosity Number (H2SO4 (Sulphuric Acid))
|
|
--
|
cm³/g
|
ISO 307 |
|
Tensile Modulus (73°F)
|
|
|
psi
|
ISO 527-2 |
|
Tensile Stress (Yield, 73°F)
|
|
|
psi
|
ISO 527-2/50 |
|
Tensile Strain (Yield, 73°F)
|
|
|
%
|
ISO 527-2/50 |
|
Nominal Tensile Strain at Break (73°F)
|
|
|
%
|
ISO 527-2/50 |
|
Flexural Modulus (73°F)
|
|
--
|
psi
|
ISO 178 |
|
Charpy Notched Impact Strength (73°F)
|
|
|
ft·lb/in²
|
ISO 179/1eA |
|
Charpy Unnotched Impact Strength (73°F)
|
|
|
|
ISO 179/1eU |
|
Notched Izod Impact Strength
|
|
|
|
ISO 180/1A |
|
-22°F
|
|
--
|
ft·lb/in²
|
|
|
73°F
|
|
|
ft·lb/in²
|
|
|
Heat Deflection Temperature
|
|
|
|
|
|
66 psi, Unannealed
|
|
--
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
|
--
|
°F
|
ISO 75-2/A |
|
Melting Temperature (DSC)
|
|
--
|
°F
|
ISO 3146 |
|
CLTE - Flow (73 to 176°F)
|
|
--
|
in/in/°F
|
ISO 11359-2 |
|
Thermal Conductivity
|
|
--
|
Btu·in/hr/ft²/°F
|
ISO 8302 |
|
Surface Resistivity
|
--
|
|
ohm
|
IEC 60093 |
|
Volume Resistivity
|
|
|
ohm·cm
|
IEC 60093 |
|
Relative Permittivity (73°F, 1 MHz)
|
|
|
|
IEC 60250 |
|
Dissipation Factor (73°F, 1 MHz)
|
|
|
|
IEC 60250 |
|
Comparative Tracking Index (Solution A)
|
|
--
|
V
|
IEC 60112 |
|
Flame Rating - UL (0.0630 in)
|
|
--
|
|
UL 94 |
|
|
The value listed as Thermal Conductivity, ISO 8302, was tested in accordance with DIN 52612-2.
Maximum Service Temperature (Short Cycle Operation): 200°C
Moisture Absorption, Equilibrium, ISO 62, 23°C, 50% RH: 2.5 to 3.1%
Specific Heat Capacity: 1700 J/(kg K)
Temperature Index at 50% Loss of Tensile Strength after 20000h, IEC 216: 99°C
Temperature Index at 50% Loss of Tensile Strength after 5000h, IEC 216: 118°C
Water Absorption, Saturation in Water, ISO 62, 23°C: 8 to 9%
|
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Ultramid® A 3SK, Ultramid A 3SK, Ultramid® A , Ultramid A, UltramidA3SK, UltramidA, A 3 SK, A3SK, A3, 3 SK, 3SK, Polyamide 66, Nylon 66, Polyamide, Nylon, pa66, BASF, Polyamide66, Nylon66, SK3, 3A
|
|
|
Generic Name may also be described by the following terms: PA66.
|
|
|
Generic Name may also be described by the following terms: PA66.
|
|
|
Features may also be described by the following terms: Good Flow, Fast Cycle, Rapid Cycle, Productivity, Fast Molding Cycle.
|
|
|
Uses may also be described by the following terms: Thin-walled Parts, Thin Walled Parts, Thin-wall Parts, Thin wall Parts, Thinwall Parts, Housings, Housing, Engineering Parts.
|
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Ultramid® A 3SK, Ultramid A 3SK, Ultramid® A , Ultramid A, UltramidA3SK, UltramidA, A 3 SK, A3SK, A3, 3 SK, 3SK, Polyamide 66, Nylon 66, Polyamide, Nylon, pa66, BASF, Polyamide66, Nylon66, SK3, 3A
|