Reny® 1313H Mitsubishi EP Polyarylamide (Glass Fiber Reinforcement, 40%)

General

Material Status

Commercial: Active

Availability

Asia Pacific

Europe

North America

Filler / Reinforcement

Glass Fiber Reinforcement, 40% Filler by Weight

Features

High Impact Resistance

Physical	Dry	Conditioned	Unit	Test Method
Density		--	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (280°C/3.8 kg)		--	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (280°C/3.8 kg)		--	in³/10min	ISO 1133
Molding Shrinkage		--	%
Water Absorption				ISO 62
Saturation, 73°F		--	%
Equilibrium, 73°F, 50% RH		--	%
Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus			psi	ISO 527-2
Tensile Stress (Break)			psi	ISO 527-2
Tensile Strain (Break)			%	ISO 527-2
Flexural Modulus			psi	ISO 178
Flexural Strength			psi	ISO 178
Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (73°F)			ft·lb/in²	ISO 179
Charpy Unnotched Impact Strength (73°F)			ft·lb/in²	ISO 179
Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
66 psi, Unannealed			°F	ISO 75-2/B
264 psi, Unannealed			°F	ISO 75-2/A
CLTE				ISO 11359-2
Flow		--	in/in/°F
Transverse		--	in/in/°F
Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity			ohm	IEC 60093
Volume Resistivity			ohm·cm	IEC 60093
Relative Permittivity				IEC 60250
100 Hz	--
1 MHz	--
Dissipation Factor				IEC 60250
100 Hz	--
1 MHz	--
Comparative Tracking Index			V	IEC 60112
Electric Strength				IEC 60243-1
0.0394 in			V/mil
0.0787 in			V/mil
Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating - UL (0.0630 in)		--		UL 94
Related Terminology
Dry	Product names can be difficult to match. You may have searched any one of these terms to find this product: Reny® 1313H, Reny 1313H, Reny® , Reny, Reny1313H, 1313 H, 1313H, Polyarylamide, PARA, Polyamide, Nylon, Mitsubishi EP, H1313
Features
Dry	Features may also be described by the following terms: High Impact Resistance.
Conditioned	Product names can be difficult to match. You may have searched any one of these terms to find this product: Reny® 1313H, Reny 1313H, Reny® , Reny, Reny1313H, 1313 H, 1313H, Polyarylamide, PARA, Polyamide, Nylon, Mitsubishi EP, H1313

Injection	Dry	Unit
Drying Temperature
A		°F
B		°F
Drying Time
A		hr
B		hr
Rear Temperature		°F
Middle Temperature		°F
Front Temperature		°F
Nozzle Temperature		°F
Mold Temperature		°F
Injection Pressure		psi
Injection Rate
Screw Speed		rpm

Notes

¹Typical properties: these are not to be construed as specifications.

Reny® 1313H

Polyarylamide

Glass Fiber Reinforcement, 40%

Supplied by Mitsubishi Engineering-Plastics Corp