VESTAMID® L1930 yellow V306160 Evonik Degussa Polyamide 12 (Milled Glass Fiber, 30%)

Product Description

Heat-stabilized, glass fiber-reinforced polyamide 12 compound

VESTAMID L1930 yellow V306160 is a heatstabilized, 30% milled glass fibers reinforced PA 12 compound suitable for injection molding.

Due to the reinforcement moldings made from this compound exhibit a high strength and rigidity. Because PA 12 absorbs only little water, the parts have a good dimensional stability and almost unaffected mechanical properties at changing ambient humidity.

Due to the reinforcement the shrinking of moldings is decreased compared with unreinforced compounds. Using specialty short glass fibers for the reinforcement of VESTAMID L1930 yellow V306160 the difference between longitudinal and transverse shrinkage relating to the flow direction of the melt is significantly lower than with common glass fibers. Therefore especially low-warpage precision parts can be molded.

As a semi-crystalline material VESTAMID L1930 yellow V306160 features an outstanding chemical resistance, e.g., against fuels, oils and fats.

General

Material Status

Commercial: Active

Availability

Europe

North America

Filler / Reinforcement

Milled Glass Fiber, 30% Filler by Weight

Additive

Heat Stabilizer

Features

Fuel Resistant

Gasoline Resistance

Good Chemical Resistance

Good Dimensional Stability

Grease Resistant

Heat Stabilized

High Rigidity

High Strength

Low Shrinkage

Low to No Water Absorption

Low Warpage

Oil Resistant

Semi Crystalline

Appearance

Yellow

Forms

Pellets

Processing Method

Injection Molding

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ISO 1183
Molding Shrinkage²			ISO 294-4
Across Flow: 176°F, 0.0787 in		%
Flow: 176°F, 0.0787 in		%
Water Absorption			ISO 62
Saturation, 73°F		%
Equilibrium, 73°F, 50% RH		%
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus		psi	ISO 527-2
Tensile Stress (Yield)		psi	ISO 527-2
Tensile Strain			ISO 527-2
Yield		%
Break		%
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-22°F, Complete Break		ft·lb/in²
73°F, Complete Break		ft·lb/in²
Charpy Unnotched Impact Strength			ISO 179/1eU
-22°F, Complete Break		ft·lb/in²
73°F, Complete Break		ft·lb/in²
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
66 psi, Unannealed		°F	ISO 75-2/B
264 psi, Unannealed		°F	ISO 75-2/A
Vicat Softening Temperature
--		°F	ISO 306/A
--		°F	ISO 306/B
Electrical	Nominal Value	Unit	Test Method
Surface Resistivity		ohm	IEC 60093
Volume Resistivity		ohm·cm	IEC 60093
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: VESTAMID® L1930 yellow V306160, VESTAMID L1930 yellow V306160, VESTAMID® , VESTAMID, VESTAMIDL1930yellowV306160, L 1930 yellow V 306160, L1930 yellow V306160, L1930, 1930yellow, yellowV, V306160, L1930yellowV306160, Polyamide 12, Nylon 12, Polyamide, Nylon, pa12, Evonik Degussa, Polyamide12, Nylon12, 1930L
Generic Name
Generic Name may also be described by the following terms: PA12.
Features
Features may also be described by the following terms: Low Water Absorption, Low Moisture Absorption, Water Resistant, Moisure Resistant, High Strength, Good Dimensional Stability, Dimensionally Stable, Good Chemical Resistance, Chemical Resistant, Semi-Crystalline, Low Warpage, Low Warp, Low Shrinkage, High Rigidity, Heat Stabilized, Heat-ageing Stabilized, Heat Ageing Stabilized, Heat-aging Stabilized, Heat Aging Stabilized.

Notes

¹Typical properties: these are not to be construed as specifications.

²determined on 2 mm sheets with film gate at rim mold temperature 80°C

VESTAMID® L1930 yellow V306160

Polyamide 12

Milled Glass Fiber, 30%

Supplied by Evonik Degussa GmbH