HAIPLEN EP100 MF6 Taro Plast Polypropylene Copolymer (Mineral Filler, 33%)

Product Description

Polypropylene copolymer high flow 33% mineral filled, high impact resistance and good mechanical properties.

General

Material Status

Availability

Filler / Reinforcement

Features

Processing Method

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)		g/10 min	ISO 1133
Molding Shrinkage			Internal Method
Across Flow		%
Flow		%
Water Absorption (73°F, 24 hr)		%	ISO 62
Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)		psi	ISO 527-2/50
Tensile Strain (Break)		%	ISO 527-2/50
Flexural Modulus²		psi	ISO 178
Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
-4°F		ft·lb/in
32°F		ft·lb/in
73°F		ft·lb/in
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (264 psi, Unannealed)		°F	ISO 75-2/A
Vicat Softening Temperature
--		°F	ISO 306/A50
--		°F	ISO 306/B50
Continuous Use Temperature - 20000 hr		°F	IEC 60216
Flammability	Nominal Value	Unit	Test Method
Flame Rating - UL (0.0630 in)			UL 94
Additional Information	Nominal Value	Unit	Test Method
Reinforcement Content³ (1112°F)		%	ISO 3451
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: HAIPLEN EP100 MF6, HAIPLEN , HAIPLENEP100MF6, EP 100 MF 6, EP100 MF6, EP100, 100MF, MF6, EP100MF6, Polypropylene Copolymer, PP Copolymer, Polypropylene, PP, Taro Plast, PolypropyleneCopolymer, PPCopolymer, 100EP
Features
Features may also be described by the following terms: High Flow, High Melt, High MFI, High Impact Resistance.

Injection	Nominal Value	Unit
Processing (Melt) Temp		°F
Mold Temperature		°F
Injection Rate
Injection Notes
Pre-heat Temperature: 70 to 80°C Pre-heat Time: 3 hr

Notes

¹Typical properties: these are not to be construed as specifications.

²0.039 in/min

³1 hr

HAIPLEN EP100 MF6