TAROMID B 280 G2 X0

Polyamide 6

Glass Fiber Reinforcement, 10%

Supplied by Taro Plast S.p.A.

The technical datasheet with complete property values for TAROMID B 280 G2 X0 is available to members of the Prospector Plastics Database.
Register to view full datasheet.
Register to View Full Datasheet
Product Description
Polyamide 6 medium viscosity 10% glass fibres reinforced, flame retardant UL94 V0, heat stabilized, good flame proofing also at low thickness, good flow and good mechanical properties.
General  
Material Status 
  • Commercial: Active
Availability 
  • Europe
Filler / Reinforcement 
  • Glass Fiber Reinforcement, 10% Filler by Weight
Additive 
  • Flame Retardant
  • Heat Stabilizer
  
Features 
  • Flame Retardant
  • Good Flow
  • Heat Stabilized
Processing Method 
  • Injection Molding
Physical
Nominal Value
Unit
Test Method
Density
g/cm³
 ISO 1183
Molding Shrinkage
     Internal Method
Across Flow
%
  
Flow
%
  
Water Absorption
     ISO 62
73°F, 24 hr
%
  
Saturation, 73°F
%
  
Granule Humidity 2
%
  
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
psi
 ISO 527-2/1
Tensile Strain (Break)
%
 ISO 527-2/50
Flexural Modulus 3
psi
 ISO 178
Flexural Strength 3
psi
 ISO 178
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength (73°F)
ft·lb/in²
 ISO 179/1eA
Notched Izod Impact (73°F)
ft·lb/in
 ASTM D256
Thermal
Nominal Value
Unit
Test Method
Heat Deflection Temperature 4 (264 psi, Unannealed)
°F
 ISO 75-2/A
Vicat Softening Temperature
      
--
°F
 ISO 306/A50
--
°F
 ISO 306/B50
Ball Pressure Test (338°F)
 
 IEC 60695-10-2
Melting Temperature
°F
 ISO 11357-3
CLTE - Flow (-22 to 86°F)
in/in/°F
 ISO 11359-2
Continuous Use Temperature
     IEC 60216
20000 hr
°F
  
Short Term
°F
  
Electrical
Nominal Value
Unit
Test Method
Volume Resistivity
ohm·cm
 IEC 60093
Comparative Tracking Index (Solution A)
V
 IEC 60112
Flammability
Nominal Value
Unit
Test Method
Flame Rating - UL (0.0382 in)
 
 UL 94
Glow Wire Flammability Index (0.0394 in)
°F
 IEC 60695-2-12
Glow Wire Ignition Temperature (0.0630 in)
°F
 IEC 60695-2-13
Oxygen Index
%
 ASTM D2863
Additional Information
Nominal Value
Unit
Test Method
Reinforcement Content 5 (1562°F)
%
 ISO 3451
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: TAROMID B 280 G2 X0, TAROMID B , TAROMIDB280G2X0, TAROMIDB, B 280 G 2 X 0, B280 G2 X0, B280, 280 G 2 X 0, B280G2X0, 280 G2 X0, 280G, G2, 2X, X0, 280G2X0, Polyamide 6, Nylon 6, Polyamide, Nylon, pa6, Taro Plast, Polyamide6, Nylon6, G280, 280B
Generic Name
Generic Name may also be described by the following terms: PA6.
Features
Features may also be described by the following terms: Heat Stabilized, Heat-ageing Stabilized, Heat Ageing Stabilized, Heat-aging Stabilized, Heat Aging Stabilized, Good Flow.
Injection
Nominal Value
Unit
 
Drying Temperature
°F
  
Drying Time
hr
  
Processing (Melt) Temp
°F
  
Mold Temperature
°F
  
Injection Rate
 
  
Injection Notes
Pre-heat Temperature: 80 to 100°C
Pre-heat Time: 3 hr
Notes
1Typical properties: these are not to be construed as specifications.
2TARO 002
30.039 in/min
4120°C/hr
51 hr
 
IDES
Copyright © 2012 IDES
The information presented on this datasheet was acquired by IDES from the producer of the material. IDES makes substantial efforts to assure the accuracy of this data. However, IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.