HAIPLEN EP150 C4 Taro Plast Polypropylene Copolymer (Calcium Carbonate Filler, 20%)

General

Material Status

Availability

Filler / Reinforcement

Features

Appearance

Processing Method

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)		g/10 min	ISO 1133
Molding Shrinkage			Internal Method
Across Flow		%
Flow		%
Granule Humidity²		%	Internal Method
Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Break)		psi	ISO 527-2/50
Tensile Strain (Break)		%	ISO 527-2/50
Flexural Modulus³		psi	ISO 178
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (73°F)		ft·lb/in²	ISO 179/1eA
Notched Izod Impact (73°F)		ft·lb/in	ASTM D256
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
66 psi, Unannealed		°F	ISO 75-2/B
264 psi, Unannealed		°F	ISO 75-2/A
Vicat Softening Temperature
--		°F	ISO 306/A50
--		°F	ISO 306/B50
Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)		V	IEC 60112
Flammability	Nominal Value	Unit	Test Method
Flame Rating - UL (0.126 in)			UL 94
Oxygen Index		%	ASTM D2863
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: HAIPLEN EP150 C4, HAIPLEN , HAIPLENEP150C4, EP 150 C 4, EP150 C4, EP150, 150C, C4, EP150C4, Polypropylene Copolymer, PP Copolymer, Polypropylene, PP, Taro Plast, PolypropyleneCopolymer, PPCopolymer, 150EP
Features
Features may also be described by the following terms: Good Surface Finish, High Flow, High Melt, High MFI.

Injection	Nominal Value	Unit
Drying Temperature - Pre-heater		°F
Drying Time - Pre-heater		hr
Processing (Melt) Temp		°F
Mold Temperature		°F
Injection Rate

Notes

¹Typical properties: these are not to be construed as specifications.

²TARO 002

³0.039 in/min

HAIPLEN EP150 C4