POLYLAC PA-717C Chi Mei Acrylonitrile Butadiene Styrene

General

Material Status

Commercial: Active

Availability

Africa & Middle East

Asia Pacific

Europe

Latin America

North America

South America

Features

General Purpose

Medium Impact Resistance

RoHS Compliance

Automotive Specifications

Forms

Pellets

Processing Method

Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity
--			ASTM D792
--		g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)		g/10 min	ASTM D1238
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg)		in³/10min	ISO 1133
Mechanical	Nominal Value	Unit	Test Method
Tensile Strength
Yield, 73°F		psi	ASTM D638
Yield		psi	ISO 527-2/50
Break		psi	ISO 527-2/50
Tensile Elongation
Break, 73°F		%	ASTM D638
Break		%	ISO 527-2/50
Flexural Modulus
73°F		psi	ASTM D790
--²		psi	ISO 178
Flexural Strength
--²		psi	ISO 178
Yield, 73°F		psi	ASTM D790
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength		ft·lb/in²	ISO 179
Charpy Unnotched Impact Strength			ISO 179
Notched Izod Impact
73°F, 0.125 in		ft·lb/in	ASTM D256
73°F, 0.250 in		ft·lb/in	ASTM D256
--		ft·lb/in²	ISO 180/1A
Unnotched Izod Impact Strength			ISO 180/1U
Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale, 0.500 in)			ASTM D785
Ball Indentation Hardness (H 358/30)		psi	ISO 2039-1
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
264 psi, Unannealed		°F	ASTM D648, ISO 75-2/A
264 psi, Annealed		°F	ASTM D648
264 psi, Annealed		°F	ISO 75-2/A
Vicat Softening Temperature
--		°F	ASTM D1525³
--		°F	ISO 306/A50
--		°F	ISO 306/A120
--		°F	ISO 306/B50
--		°F	ISO 306/B120
Electrical	Nominal Value	Unit	Test Method
Volume Resistivity		ohm·cm	IEC 60093
Arc Resistance (PLC)			ASTM D495
Flammability	Nominal Value	Unit	Test Method
Flame Rating - UL			UL 94
0.0591 in, ALL
0.0625 in
0.118 in, ALL
UL File Number
UL	Nominal Value	Unit	Test Method
RTI Str			UL 746
0.0591 in		°F
0.118 in		°F
RTI Imp			UL 746
0.0591 in		°F
0.118 in		°F
RTI Elec			UL 746
0.0591 in		°F
0.118 in		°F
Comparative Tracking Index (CTI) (PLC)			UL 746
High Voltage Arc Tracking Rate (HVTR) (PLC)			UL 746
Hot-wire Ignition (HWI) (PLC)			UL 746
0.0591 in
0.118 in
High Amp Arc Ignition (HAI) (PLC)			UL 746
0.0591 in
0.118 in
Additional Information
Impact Flexural Test, ISO 179/2C, Notched: 14 kJ/m² Impact Flexural Test, ISO 179/2D, Unnotched: No Break
Related Terminology
This supplier and product may also be known by these terms: ChiMei Product names can be difficult to match. You may have searched any one of these terms to find this product: POLYLAC® PA-717C, POLYLAC PA717C, POLYLAC® , POLYLAC, POLYLACPA717C, PA, PA 717 C, PA-717C, PA717C, PA:717C, PA/717C, PA+717C, PA_717C, PA 717C, PA717, 717C, Acrylonitrile Butadiene Styrene, ABS, Chi Mei, AcrylonitrileButadieneStyrene, 717PA
Features
Features may also be described by the following terms: Medium Impact Resistance.
Automotive Specifications
This plastic material has approval for 3 automotive specifications from the following agencies (the number in parentheses shows the number of specifications for that agency): GM (1), DELPHI (2).

Injection	Nominal Value	Unit
Drying Temperature		°F
Drying Time		hr
Rear Temperature		°F
Middle Temperature		°F
Front Temperature		°F
Mold Temperature		°F

Notes

¹Typical properties: these are not to be construed as specifications.

²0.079 in/min

³Rate A (50°C/h)

POLYLAC® PA-717C

Acrylonitrile Butadiene Styrene

Supplied by CHI MEI CORPORATION