Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
|
|
ASTM D1238 |
|
200°C/10.0 kg
|
|
g/10 min
|
|
|
200°C/5.0 kg
|
|
g/10 min
|
|
|
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg)
|
|
in³/10min
|
ISO 1133 |
|
Tensile Stress
|
|
|
|
|
Yield
|
|
psi
|
ISO 527-2/50 |
|
Break
|
|
psi
|
ISO 527-2/50 |
|
0.125 in 2
|
|
psi
|
ASTM D638 |
|
Tensile Elongation
|
|
|
|
|
Break, 0.125 in 2
|
|
%
|
ASTM D638 |
|
Break
|
|
%
|
ISO 527-2/50 |
|
Flexural Modulus
|
|
|
|
|
0.250 in 3
|
|
psi
|
ASTM D790 |
|
-- 4
|
|
psi
|
ISO 178 |
|
Flexural Strength
|
|
|
|
|
0.250 in 5
|
|
psi
|
ASTM D790 |
|
-- 4
|
|
psi
|
ISO 178 |
|
Charpy Notched Impact Strength
|
|
ft·lb/in²
|
ISO 179 |
|
Charpy Unnotched Impact Strength
|
|
|
ISO 179 |
|
Notched Izod Impact
|
|
|
|
|
73°F, 0.125 in
|
|
ft·lb/in
|
ASTM D256 |
|
73°F, 0.250 in
|
|
ft·lb/in
|
ASTM D256 |
|
--
|
|
ft·lb/in²
|
ISO 180/1A |
|
Unnotched Izod Impact Strength
|
|
|
ISO 180/1U |
|
Rockwell Hardness (R-Scale, 0.500 in)
|
|
|
ASTM D785 |
|
Ball Indentation Hardness (H 358/30)
|
|
psi
|
ISO 2039-1 |
|
Deflection Temperature Under Load
|
|
|
|
|
264 psi, Unannealed
|
|
°F
|
ASTM D648, ISO 75-2/A |
|
264 psi, Annealed
|
|
°F
|
ASTM D648 |
|
264 psi, Annealed
|
|
°F
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ASTM D1525 6, ISO 306/A120 6 |
|
--
|
|
°F
|
ISO 306/A50 |
|
--
|
|
°F
|
ISO 306/B50 |
|
--
|
|
°F
|
ISO 306/B120 |
|
Arc Resistance (PLC)
|
|
|
ASTM D495 |
|
Flame Rating - UL
|
|
|
UL 94 |
|
0.0591 in, ALL
|
|
|
|
|
0.0626 in
|
|
|
|
|
0.118 in, ALL
|
|
|
|
|
UL File Number
|
|
|
|
|
RTI Str
|
|
|
UL 746 |
|
0.0591 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
RTI Imp
|
|
|
UL 746 |
|
0.0591 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
RTI Elec
|
|
|
UL 746 |
|
0.0591 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
Comparative Tracking Index (CTI) (PLC)
|
|
|
UL 746 |
|
High Voltage Arc Tracking Rate (HVTR) (PLC)
|
|
|
UL 746 |
|
Hot-wire Ignition (HWI) (PLC)
|
|
|
UL 746 |
|
0.0591 in
|
|
|
|
|
0.118 in
|
|
|
|
|
High Amp Arc Ignition (HAI) (PLC)
|
|
|
UL 746 |
|
0.0591 in
|
|
|
|
|
0.118 in
|
|
|
|
|
Impact Flexural Test, ISO 179/2C, Notched: 20 kJ/m²
Impact Flexural Test, ISO 179/2D, Unnotched: No Break
|
|
This supplier and product may also be known by these terms: ChiMei
Product names can be difficult to match. You may have searched any one of these terms to find this product: POLYLAC® PA-747, POLYLAC PA747, POLYLAC® , POLYLAC, POLYLACPA747, PA, PA-747, PA747, PA:747, PA/747, PA+747, PA_747, PA 747, Acrylonitrile Butadiene Styrene, ABS, Chi Mei, AcrylonitrileButadieneStyrene, 747PA
|
|
Features may also be described by the following terms: High Impact Resistance.
|
|