| Specific Gravity |
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) |
|
g/10 min
|
ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) |
|
in³/10min
|
ISO 1133 |
| Tensile Strength |
|
|
|
|
Yield, 0.125 in 2
|
|
psi
|
ASTM D638 |
|
Yield
|
|
psi
|
ISO 527-2/50 |
|
Break
|
|
psi
|
ISO 527-2/50 |
| Tensile Elongation |
|
|
|
|
Break, 0.125 in 2
|
|
%
|
ASTM D638 |
|
Break
|
|
%
|
ISO 527-2/50 |
| Flexural Modulus |
|
|
|
|
0.250 in 3
|
|
psi
|
ASTM D790 |
|
-- 4
|
|
psi
|
ISO 178 |
| Flexural Strength |
|
|
|
|
0.250 in 3
|
|
psi
|
ASTM D790 |
|
-- 4
|
|
psi
|
ISO 178 |
| Charpy Notched Impact Strength |
|
ft·lb/in²
|
ISO 179 |
| Charpy Unnotched Impact Strength |
|
|
ISO 179 |
| Notched Izod Impact |
|
|
|
|
73°F, 0.125 in
|
|
ft·lb/in
|
ASTM D256 |
|
73°F, 0.250 in
|
|
ft·lb/in
|
ASTM D256 |
|
--
|
|
ft·lb/in²
|
ISO 180/1A |
| Unnotched Izod Impact Strength |
|
|
ISO 180/1U |
| Rockwell Hardness (R-Scale, 0.500 in) |
|
|
ASTM D785 |
| Ball Indentation Hardness (H 358/30) |
|
psi
|
ISO 2039-1 |
| Deflection Temperature Under Load |
|
|
|
|
264 psi, Unannealed, 0.250 in
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed
|
|
°F
|
ISO 75-2/A |
|
264 psi, Annealed, 0.250 in
|
|
°F
|
ASTM D648 |
|
264 psi, Annealed
|
|
°F
|
ISO 75-2/A |
| Vicat Softening Temperature |
|
|
|
|
--
|
|
°F
|
ASTM D1525 5 |
|
--
|
|
°F
|
ISO 306/A50 |
|
--
|
|
°F
|
ISO 306/A120 |
|
--
|
|
°F
|
ISO 306/B50 |
|
--
|
|
°F
|
ISO 306/B120 |
| Volume Resistivity |
|
ohm·cm
|
ASTM D257 |
| Arc Resistance (PLC) |
|
|
ASTM D495 |
| Flame Rating - UL |
|
|
UL 94 |
|
0.0591 in, ALL
|
|
|
|
|
0.0626 in
|
|
|
|
|
0.118 in, ALL
|
|
|
|
| UL File Number |
|
|
|
| RTI Str |
|
|
UL 746 |
|
0.0591 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
| RTI Imp |
|
|
UL 746 |
|
0.0591 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
| RTI Elec |
|
|
UL 746 |
|
0.0591 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
| Comparative Tracking Index (CTI) (PLC) |
|
|
UL 746 |
| High Voltage Arc Tracking Rate (HVTR) (PLC) |
|
|
UL 746 |
| Hot-wire Ignition (HWI) (PLC) |
|
|
UL 746 |
|
0.0591 in
|
|
|
|
|
0.118 in
|
|
|
|
| High Amp Arc Ignition (HAI) (PLC) |
|
|
UL 746 |
|
0.0591 in
|
|
|
|
|
0.118 in
|
|
|
|
|
Impact Flexural Test, ISO 179/2C, Notched: 21 kJ/m²
Impact Flexural Test, ISO 179/2D, Unnotched: No Break
|
|
This supplier and product may also be known by these terms: ChiMei
Product names can be difficult to match. You may have searched any one of these terms to find this product: POLYLAC® PA-709, POLYLAC PA709, POLYLAC® , POLYLAC, POLYLACPA709, PA, PA-709, PA709, PA:709, PA/709, PA+709, PA_709, PA 709, Acrylonitrile Butadiene Styrene, ABS, Chi Mei, AcrylonitrileButadieneStyrene, 709PA
|
|
Features may also be described by the following terms: High Impact Resistance.
|
|
Uses may also be described by the following terms: Piping, Pipe.
|