Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
|
--
|
|
g/cm³
|
ASTM D792 |
|
Specific Volume
|
|
in³/lb
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR)
|
|
|
ASTM D1238 |
|
300°C/1.2 kg
|
|
g/10 min
|
|
|
300°C/5.0 kg
|
|
g/10 min
|
|
|
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg)
|
|
in³/10min
|
ISO 1133 |
|
Molding Shrinkage
|
|
|
Internal Method |
|
Flow 2
|
|
in/in
|
|
|
Flow: 0.126 in
|
|
in/in
|
|
|
Across Flow: 0.126 in
|
|
in/in
|
|
|
Water Absorption
|
|
|
|
|
24 hr
|
|
%
|
ASTM D570 |
|
Saturation, 73°F
|
|
%
|
ISO 62 |
|
Equilibrium, 73°F
|
|
%
|
ASTM D570 |
|
Equilibrium, 212°F
|
|
%
|
ASTM D570 |
|
Equilibrium, 73°F, 50% RH
|
|
%
|
ISO 62 |
|
Tensile Modulus
|
|
|
|
|
-- 3
|
|
psi
|
ASTM D638 |
|
--
|
|
psi
|
ISO 527-2/1 |
|
Tensile Strength
|
|
|
|
|
Yield 4
|
|
psi
|
ASTM D638 |
|
Yield
|
|
psi
|
ISO 527-2/50 |
|
Break 4
|
|
psi
|
ASTM D638 |
|
Break
|
|
psi
|
ISO 527-2/50 |
|
Tensile Elongation
|
|
|
|
|
Yield 4
|
|
%
|
ASTM D638 |
|
Yield
|
|
%
|
ISO 527-2/50 |
|
Break 4
|
|
%
|
ASTM D638 |
|
Break
|
|
%
|
ISO 527-2/50 |
|
Flexural Modulus
|
|
|
|
|
1.97 in Span 5
|
|
psi
|
ASTM D790 |
|
-- 6
|
|
psi
|
ISO 178 |
|
Flexural Strength
|
|
|
|
|
-- 6, 7
|
|
psi
|
ISO 178 |
|
Yield, 1.97 in Span 5
|
|
psi
|
ASTM D790 |
|
Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel)
|
|
mg
|
ASTM D1044 |
|
Charpy Notched Impact Strength 8 (73°F)
|
|
ft·lb/in²
|
ISO 179/1eA |
|
Notched Izod Impact
|
|
|
|
|
-22°F
|
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
|
ft·lb/in
|
ASTM D256 |
|
-22°F 9
|
|
ft·lb/in²
|
ISO 180/1A |
|
73°F 9
|
|
ft·lb/in²
|
ISO 180/1A |
|
Unnotched Izod Impact (73°F)
|
|
ft·lb/in
|
ASTM D4812 |
|
Instrumented Dart Impact
|
|
|
ASTM D3763 |
|
73°F, Energy at Peak Load
|
|
in·lb
|
|
|
73°F, Total Energy
|
|
in·lb
|
|
|
Gardner Impact (73°F)
|
|
in·lb
|
ASTM D3029 |
|
Tensile Impact Strength 10
|
|
ft·lb/in²
|
ASTM D1822 |
|
Rockwell Hardness
|
|
|
ASTM D785 |
|
M-Scale
|
|
|
|
|
R-Scale
|
|
|
|
|
Deflection Temperature Under Load
|
|
|
|
|
66 psi, Unannealed, 0.126 in
|
|
°F
|
ASTM D648 |
|
66 psi, Unannealed, 0.252 in
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed, 0.126 in
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed, 0.252 in
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed, 2.52 in Span 11
|
|
°F
|
ISO 75-2/Af |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ASTM D1525 12 |
|
--
|
|
°F
|
ISO 306/B50 |
|
--
|
|
°F
|
ISO 306/B120 |
|
Ball Pressure Test (167°F)
|
|
|
IEC 60695-10-2 |
|
CLTE
|
|
|
|
|
Flow: -40 to 104°F
|
|
in/in/°F
|
ASTM E831 |
|
Flow: -40 to 203°F
|
|
in/in/°F
|
ASTM E831 |
|
Flow: -40 to 104°F
|
|
in/in/°F
|
ISO 11359-2 |
|
Transverse: -40 to 104°F
|
|
in/in/°F
|
ASTM E831 |
|
Transverse: -40 to 104°F
|
|
in/in/°F
|
ISO 11359-2 |
|
Specific Heat
|
|
Btu/lb/°F
|
ASTM C351 |
|
Thermal Conductivity
|
|
Btu·in/hr/ft²/°F
|
ASTM C177 |
|
Volume Resistivity
|
|
ohm·cm
|
ASTM D257 |
|
Dielectric Strength (0.126 in, in Air)
|
|
V/mil
|
ASTM D149 |
|
Dielectric Constant
|
|
|
ASTM D150 |
|
50 Hz
|
|
|
|
|
60 Hz
|
|
|
|
|
1 MHz
|
|
|
|
|
Dissipation Factor
|
|
|
ASTM D150 |
|
50 Hz
|
|
|
|
|
60 Hz
|
|
|
|
|
1 MHz
|
|
|
|
|
Flame Rating - UL (0.0579 in)
|
|
|
UL 94 |
|
RTI Str
|
|
°F
|
UL 746 |
|
RTI Imp
|
|
°F
|
UL 746 |
|
RTI Elec
|
|
°F
|
UL 746 |
|
Comparative Tracking Index (CTI) (PLC)
|
|
|
UL 746 |
|
High Voltage Arc Tracking Rate (HVTR) (PLC)
|
|
|
UL 746 |
|
Hot-wire Ignition (HWI) (PLC)
|
|
|
UL 746 |
|
High Amp Arc Ignition (HAI) (PLC)
|
|
|
UL 746 |
|
Refractive Index
|
|
|
ASTM D542 |
|
Transmittance (100 mil)
|
|
%
|
ASTM D1003 |
|
Haze (100 mil)
|
|
%
|
ASTM D1003 |
|
This supplier and product may also be known by these terms: GE Plastics, LNP Engineering Plastics, GE Polymerland
Product names can be difficult to match. You may have searched any one of these terms to find this product: LEXAN* 104 Resin, LEXAN 104 Resin, LEXAN* , LEXAN, LEXAN104Resin, 104 Resin, 104Resin, Polycarbonate, PC, SABIC IP, Resin104
|
|
This plastic material has 1 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): FDA (1).
|