Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
|
Specific Volume
|
|
in³/lb
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR) (250°C/5.0 kg)
|
|
g/10 min
|
ASTM D1238 |
|
Melt Volume-Flow Rate (MVR) (250°C/5.0 kg)
|
|
in³/10min
|
ISO 1133 |
|
Molding Shrinkage
|
|
|
Internal Method |
|
Flow 2
|
|
in/in
|
|
|
Flow 3
|
|
in/in
|
|
|
Flow 4
|
|
in/in
|
|
|
Flow: 0.126 in
|
|
in/in
|
|
|
Across Flow 2
|
|
in/in
|
|
|
Across Flow 3
|
|
in/in
|
|
|
Across Flow 5
|
|
in/in
|
|
|
Across Flow: 0.126 in
|
|
in/in
|
|
|
Water Absorption
|
|
|
|
|
24 hr
|
|
%
|
ASTM D570 |
|
Saturation, 73°F
|
|
%
|
ISO 62 |
|
Equilibrium, 73°F, 50% RH
|
|
%
|
ISO 62 |
|
Tensile Modulus
|
|
|
|
|
-- 6
|
|
psi
|
ASTM D638 |
|
--
|
|
psi
|
ISO 527-2/1 |
|
Tensile Strength
|
|
|
|
|
Yield 7
|
|
psi
|
ASTM D638 |
|
Yield
|
|
psi
|
ISO 527-2/5 |
|
Break 7
|
|
psi
|
ASTM D638 |
|
Break
|
|
psi
|
ISO 527-2/5 |
|
Tensile Elongation
|
|
|
|
|
Yield 7
|
|
%
|
ASTM D638 |
|
Yield
|
|
%
|
ISO 527-2/5 |
|
Break 7
|
|
%
|
ASTM D638 |
|
Break
|
|
%
|
ISO 527-2/5 |
|
Flexural Modulus
|
|
|
|
|
1.97 in Span 8
|
|
psi
|
ASTM D790 |
|
-- 9
|
|
psi
|
ISO 178 |
|
Flexural Strength
|
|
|
|
|
--
|
|
psi
|
ISO 178 |
|
Break, 1.97 in Span 8
|
|
psi
|
ASTM D790 |
|
Charpy Notched Impact Strength 10
|
|
|
ISO 179/1eA |
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Charpy Unnotched Impact Strength 10
|
|
|
ISO 179/1eU |
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Notched Izod Impact
|
|
|
|
|
-22°F
|
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
|
ft·lb/in
|
ASTM D256 |
|
-22°F 11
|
|
ft·lb/in²
|
ISO 180/1A |
|
73°F 11
|
|
ft·lb/in²
|
ISO 180/1A |
|
Unnotched Izod Impact
|
|
|
|
|
73°F
|
|
ft·lb/in
|
ASTM D4812 |
|
-22°F 11
|
|
ft·lb/in²
|
ISO 180/1U |
|
73°F 11
|
|
ft·lb/in²
|
ISO 180/1U |
|
Instrumented Dart Impact (73°F, Total Energy)
|
|
in·lb
|
ASTM D3763 |
|
Rockwell Hardness (R-Scale)
|
|
|
ASTM D785, ISO 2039-2 |
|
Ball Indentation Hardness (H 358/30)
|
|
psi
|
ISO 2039-1 |
|
Deflection Temperature Under Load
|
|
|
|
|
66 psi, Unannealed, 0.126 in
|
|
°F
|
ASTM D648 |
|
66 psi, Unannealed, 0.252 in
|
|
°F
|
ASTM D648 |
|
66 psi, Unannealed, 2.52 in Span 12
|
|
°F
|
ISO 75-2/Bf |
|
264 psi, Unannealed, 0.126 in
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed, 0.252 in
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed, 2.52 in Span 12
|
|
°F
|
ISO 75-2/Af |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ASTM D1525 13, ISO 306/B50, ISO 306/B120 |
|
--
|
|
°F
|
ISO 306/A50 |
|
Ball Pressure Test (257°F)
|
|
|
IEC 60695-10-2 |
|
CLTE
|
|
|
|
|
Flow: -40 to 104°F
|
|
in/in/°F
|
ASTM E831, ISO 11359-2 |
|
Flow: 140 to 280°F
|
|
in/in/°F
|
ASTM E831 |
|
Transverse: -40 to 104°F
|
|
in/in/°F
|
ASTM E831, ISO 11359-2 |
|
Thermal Conductivity
|
|
Btu·in/hr/ft²/°F
|
ISO 8302 |
|
Volume Resistivity
|
|
ohm·cm
|
ASTM D257 |
|
Dielectric Strength
|
|
|
ASTM D149 |
|
0.0630 in, in Oil
|
|
V/mil
|
|
|
0.126 in, in Air
|
|
V/mil
|
|
|
Dielectric Constant
|
|
|
ASTM D150 |
|
100 Hz
|
|
|
|
|
1 MHz
|
|
|
|
|
Dissipation Factor
|
|
|
ASTM D150 |
|
100 Hz
|
|
|
|
|
1 MHz
|
|
|
|
|
Arc Resistance (PLC) 14
|
|
|
ASTM D495 |
|
Flame Rating - UL
|
|
|
UL 94 |
|
0.0157 in
|
|
|
|
|
0.0280 in
|
|
|
|
|
0.0787 in
|
|
|
|
|
Oxygen Index
|
|
%
|
ASTM D2863 |
|
RTI Str
|
|
°F
|
UL 746 |
|
RTI Imp
|
|
°F
|
UL 746 |
|
RTI Elec
|
|
°F
|
UL 746 |
|
Comparative Tracking Index (CTI) (PLC)
|
|
|
UL 746 |
|
High Voltage Arc Tracking Rate (HVTR) (PLC)
|
|
|
UL 746 |
|
Hot-wire Ignition (HWI) (PLC)
|
|
|
UL 746 |
|
High Amp Arc Ignition (HAI) (PLC)
|
|
|
UL 746 |
|
Outdoor Suitability
|
|
|
UL 746C |
|
This supplier and product may also be known by these terms: GE Plastics, LNP Engineering Plastics, GE Polymerland
Product names can be difficult to match. You may have searched any one of these terms to find this product: VALOX* 420SE0U Resin, VALOX 420SE0U Resin, VALOX* , VALOX, VALOX420SE0UResin, 420 SE 0 U Resin, 420SE0U Resin, 420SE, SE0, 0U, UResin, 420SE0UResin, Polybutylene Terephthalate, PBT, Polyester, SABIC IP, PolybutyleneTerephthalate, SE420
|