XENOY* 5720U Resin

Polycarbonate + PBT

Supplied by SABIC Innovative Plastics

The technical datasheet with complete property values for XENOY* 5720U Resin is available to members of the Prospector Plastics Database.
Register to view full datasheet.
Register to View Full Datasheet
Product Description
Unfilled PBT+PC alloy. Outstanding low temperature impact/chemical resistance. UV stabilized version of XENOY
General  
Material Status 
  • Commercial: Active
Availability 
  • North America
Additive 
  • UV Stabilizer
Features 
  • Good Chemical Resistance
  • Low Temperature Impact Resistance
  
Processing Method 
  • Injection Molding
Physical
Nominal Value
Unit
Test Method
Specific Gravity
      
--
 
 ASTM D792
--
g/cm³
 ISO 1183, ASTM D792
Specific Volume
in³/lb
 ASTM D792
Melt Mass-Flow Rate (MFR)
      
250°C/2.16 kg
g/10 min
 ASTM D1238, ISO 1133
250°C/5.0 kg
g/10 min
 ASTM D1238, ISO 1133
265°C/2.16 kg
g/10 min
 ASTM D1238
266°C/5.0 kg
g/10 min
 ASTM D1238
Melt Volume-Flow Rate (MVR)
     ISO 1133
250°C/2.16 kg
in³/10min
  
250°C/5.0 kg
in³/10min
  
265°C/2.16 kg
in³/10min
  
265°C/5.0 kg
in³/10min
  
Molding Shrinkage - Flow (0.126 in)
in/in
 Internal Method
Water Absorption
     ISO 62
Saturation, 73°F
%
  
Equilibrium, 73°F, 50% RH
%
  
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
      
-- 2
psi
 ASTM D638
-- 3
psi
 Internal Method
-- 4
psi
 ASTM D638
--
psi
 ISO 527-2/1
Tensile Strength
      
Yield 5
psi
 ASTM D638
Yield 6
psi
 Internal Method
Yield 7
psi
 ASTM D638
Yield
psi
 ISO 527-2/5
Yield
psi
 ISO 527-2/50
Break 5
psi
 ASTM D638
Break 6
psi
 Internal Method
Break 7
psi
 ASTM D638
Break
psi
 ISO 527-2/5, ISO 527-2/50
Tensile Elongation
      
Yield 5
%
 ASTM D638
Yield 6
%
 Internal Method
Yield 7
%
 ASTM D638
Yield
%
 ISO 527-2/5
Yield
%
 ISO 527-2/50
Break 5
%
 ASTM D638
Break 6
%
 Internal Method
Break 7
%
 ASTM D638
Break
%
 ISO 527-2/5
Break
%
 ISO 527-2/50
Flexural Modulus
      
1.97 in Span 8
psi
 ASTM D790
-- 9
psi
 ISO 178
Flexural Strength
      
-- 9, 10
psi
 ISO 178
Yield, 1.97 in Span 8
psi
 ASTM D790
Break, 1.97 in Span 8
psi
 ASTM D790
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength 11
     ISO 179/1eA
-22°F
ft·lb/in²
  
73°F
ft·lb/in²
  
Notched Izod Impact
      
-40°F
ft·lb/in
 ASTM D256
-22°F
ft·lb/in
 ASTM D256
-4°F
ft·lb/in
 ASTM D256
14°F
ft·lb/in
 ASTM D256
32°F
ft·lb/in
 ASTM D256
73°F
ft·lb/in
 ASTM D256
-40°F 12
ft·lb/in²
 ISO 180/1A
-22°F 12
ft·lb/in²
 ISO 180/1A
-4°F 12
ft·lb/in²
 ISO 180/1A
14°F 12
ft·lb/in²
 ISO 180/1A
32°F 12
ft·lb/in²
 ISO 180/1A
73°F 12
ft·lb/in²
 ISO 180/1A
Instrumented Dart Impact
     ASTM D3763
-40°F, Energy at Peak Load
in·lb
  
-40°F, Total Energy
in·lb
  
-22°F, Energy at Peak Load
in·lb
  
-22°F, Total Energy
in·lb
  
-4°F, Energy at Peak Load
in·lb
  
-4°F, Total Energy
in·lb
  
73°F, Energy at Peak Load
in·lb
  
73°F, Total Energy
in·lb
  
Thermal
Nominal Value
Unit
Test Method
Deflection Temperature Under Load
      
66 psi, Unannealed, 0.126 in
°F
 ASTM D648
66 psi, Unannealed, 0.252 in
°F
 ASTM D648
66 psi, Unannealed, 2.52 in Span 13
°F
 ISO 75-2/Bf
264 psi, Unannealed, 0.126 in
°F
 ASTM D648
264 psi, Unannealed, 0.252 in
°F
 ASTM D648
264 psi, Unannealed, 2.52 in Span 13
°F
 ISO 75-2/Af
Vicat Softening Temperature
      
--
°F
 ASTM D1525 14, ISO 306/B50 14
--
°F
 ISO 306/B120
CLTE
      
Flow: -40 to 203°F
in/in/°F
 ASTM E831
Flow: -22 to 176°F
in/in/°F
 ISO 11359-2
Transverse: -40 to 203°F
in/in/°F
 ASTM E831
Transverse: -22 to 176°F
in/in/°F
 ISO 11359-2
Related Terminology
This supplier and product may also be known by these terms: GE Plastics, LNP Engineering Plastics, GE Polymerland

Product names can be difficult to match. You may have searched any one of these terms to find this product: XENOY* 5720U Resin, XENOY 5720U Resin, XENOY* , XENOY, XENOY5720UResin, 5720 U Resin, 5720U Resin, 5720U, UResin, 5720UResin, Polycarbonate + PBT, Polycarbonate PBT, Polycarbonate : PBT, Polycarbonate / PBT, Polycarbonate - PBT, Polycarbonate _ PBT, Polycarbonate PBT, PC+PBT, PCPBT, PC:PBT, PC/PBT, PC-PBT, PC_PBT, PC PBT, Polycarbonate, PC, SABIC IP, PolycarbonatePBT, Polycarbonate_PBT, U5720
Features
Features may also be described by the following terms: Good Chemical Resistance, Chemical Resistant, Low Temperatuer Impact Resistance, Low Temp Impact Resistance.
Injection
Nominal Value
Unit
 
Drying Temperature
°F
  
Drying Time
hr
  
Drying Time, Maximum
hr
  
Suggested Max Moisture
%
  
Suggested Shot Size
%
  
Rear Temperature
°F
  
Middle Temperature
°F
  
Front Temperature
°F
  
Nozzle Temperature
°F
  
Processing (Melt) Temp
°F
  
Mold Temperature
°F
  
Back Pressure
psi
  
Screw Speed
rpm
  
Vent Depth
in
  
Notes
1Typical properties: these are not to be construed as specifications.
20.20 in/min
30.39 in/min
42.0 in/min
5Type I, 0.20 in/min
6Type I, 0.39 in/min
7Type I, 2.0 in/min
80.051 in/min
90.079 in/min
10Yield
1180*10*4 sp=62mm
1280*10*4
1380*10*4 mm
14Rate B (120°C/h), Loading 2 (50 N)
 
IDES
Copyright © 2012 IDES
The information presented on this datasheet was acquired by IDES from the producer of the material. IDES makes substantial efforts to assure the accuracy of this data. However, IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.