BCC Resins BC 8001

BCC Kwik Kast/Black is a two component, fast setting polyurethane reproduction plastic. BC 8001 sets to a demoldable hardness within 30 minutes @ 77°F. Uses include; tracing models core boxes, duplicating aids, patterns, prototypes, low temperature vacuum form tools, etc.

Handling Properties:
BCC's Kwik Kast/Black is a fast-setting, two part casting system which requires careful preparation prior to mixing parts A and B. Because Kwik Kast/Black contains components of high density there will be some separation at the bottom of each container. Using a paint shaker, jiffy mixer, or mixing spatula, re-suspension of the ingredients is easily accomplished. Precaution should be taken to prevent any moisture contamination from containers or utensils. It is recommended that the work area be well ventilated and normal cleanliness and safety rules be observed. Avoid prolonged exposure to vapors and contact with skin.

Preparation of Mold Surface:
Clean the surface from dust and possible presence of moisture. Apply BC 87 Parting Agent and polish to a uniform high gloss finish (usually 2-3 coats are recommended). For plaster or wood surfaces seal with PVC sealer to ensure complete absence of moisture, followed by 2-3 coats of 87 Parting Agent.

Mixing and Pouring:
Although not necessary, best results are obtained by evacuation of each component under 29 inches of vacuum which removes entrapped air prior to blending the two components. Pour weighed or measured amounts of Part A & B into a separate dry container by pouring Part A into Part B. Mix with a spatula or mechanical stirrer for 30-40 seconds for quart size batches or 40-50 seconds for gallon batches while avoiding air entrapment. Immediately pour mixed resin uninterrupted from a convenient height above the mold cavity. Clean your mixing tools by rinsing in an alcohol type solvent. Larger masses (2 feet or more) may be built up with successive pours. Castings may be demolded within 30-60 minutes but should be properly supported while "green". Under normal conditions, maximum hardness or cure will be achieved in 12-18 hours.