Specific Gravity
|
|
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
|
|
g/10 min
|
ASTM D1238 |
|
Coefficient of Friction
|
|
|
ASTM D1894 |
|
Film Thickness - Tested
|
|
mil
|
|
|
Film Thickness - Recommended / Available
|
|
|
|
|
Secant Modulus
|
|
|
ASTM D882 |
|
1% Secant, MD: 1.5 mil, Blown Film
|
|
psi
|
|
|
1% Secant, TD: 1.5 mil, Blown Film
|
|
psi
|
|
|
Tensile Strength
|
|
|
ASTM D882 |
|
MD: Yield, 1.5 mil, Blown Film
|
|
psi
|
|
|
TD: Yield, 1.5 mil, Blown Film
|
|
psi
|
|
|
MD: Break, 1.5 mil, Blown Film
|
|
psi
|
|
|
TD: Break, 1.5 mil, Blown Film
|
|
psi
|
|
|
Tensile Elongation
|
|
|
ASTM D882 |
|
MD: Break, 1.5 mil, Blown Film
|
|
%
|
|
|
TD: Break, 1.5 mil, Blown Film
|
|
%
|
|
|
Dart Drop Impact (1.5 mil, Blown Film)
|
|
g
|
ASTM D1709A |
|
Elmendorf Tear Strength
|
|
|
ASTM D1922 |
|
MD: 1.5 mil, Blown Film
|
|
g
|
|
|
TD: 1.5 mil, Blown Film
|
|
g
|
|
|
Oxygen Permeability 2 (73°F, Blown Film)
|
|
cm³/100 in²/24 hr
|
ASTM D1434 |
|
Water Vapor Transmission Rate (100°F, 1.5 mil, Blown Film, 100% RH)
|
|
g/100 in²/24 hr
|
ASTM F1249 |
|
Durometer Hardness (Shore D)
|
|
|
ASTM D2240 |
|
Vicat Softening Temperature
|
|
°F
|
ASTM D1525 |
|
Low Friction Puncture - Blown Film
|
|
ft·lb/in
|
Internal Method |
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: SCLAIR® 15A, SCLAIR 15A, SCLAIR® , SCLAIR, SCLAIR15A, 15 A, 15A, Polyethylene, High Density, Polyethylene High Density, HDPE, Polyethylene, PE, Nova Chemicals, PolyethyleneHighDensity, A15
|
|
Features may also be described by the following terms: Low Gel, Good Toughness, Tough, Good Strength, Butene Comonomer.
|
|
This plastic material has 1 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): FDA (1).
|