Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (250°C/5.0 kg)
|
|
g/10 min
|
ASTM D1238 |
|
Melt Volume-Flow Rate (MVR) (250°C/5.0 kg)
|
|
in³/10min
|
ISO 1133 |
|
Molding Shrinkage
|
|
|
Internal Method |
|
Flow 2
|
|
in/in
|
|
|
Flow: 0.126 in
|
|
in/in
|
|
|
Across Flow 2
|
|
in/in
|
|
|
Water Absorption
|
|
|
ISO 62 |
|
Saturation, 73°F
|
|
%
|
|
|
Equilibrium, 73°F, 50% RH
|
|
%
|
|
|
Tensile Modulus
|
|
|
|
|
-- 3
|
|
psi
|
ASTM D638 |
|
--
|
|
psi
|
ISO 527-2/1 |
|
Tensile Strength
|
|
|
|
|
Yield 4
|
|
psi
|
ASTM D638 |
|
Yield
|
|
psi
|
ISO 527-2/50 |
|
Break 4
|
|
psi
|
ASTM D638 |
|
Break
|
|
psi
|
ISO 527-2/50 |
|
Tensile Elongation
|
|
|
|
|
Yield 4
|
|
%
|
ASTM D638 |
|
Yield
|
|
%
|
ISO 527-2/50 |
|
Break 4
|
|
%
|
ASTM D638 |
|
Break
|
|
%
|
ISO 527-2/50 |
|
Flexural Modulus
|
|
|
|
|
1.97 in Span 5
|
|
psi
|
ASTM D790 |
|
-- 6
|
|
psi
|
ISO 178 |
|
Flexural Strength
|
|
|
|
|
-- 6, 7
|
|
psi
|
ISO 178 |
|
Yield, 1.97 in Span 5
|
|
psi
|
ASTM D790 |
|
Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel)
|
|
mg
|
Internal Method |
|
Charpy Notched Impact Strength
|
|
|
|
|
-22°F 8
|
|
ft·lb/in²
|
ISO 179/1eA |
|
73°F 8
|
|
ft·lb/in²
|
ISO 179/1eA |
|
73°F
|
|
ft·lb/in²
|
ISO 179/2C |
|
Charpy Unnotched Impact Strength 8
|
|
|
ISO 179/1eU |
|
-22°F
|
|
|
|
|
73°F
|
|
|
|
|
Notched Izod Impact
|
|
|
|
|
-22°F
|
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
|
ft·lb/in
|
ASTM D256 |
|
-22°F 9
|
|
ft·lb/in²
|
ISO 180/1A |
|
73°F 9
|
|
ft·lb/in²
|
ISO 180/1A |
|
Unnotched Izod Impact Strength 9
|
|
|
ISO 180/1U |
|
-22°F
|
|
|
|
|
73°F
|
|
|
|
|
Instrumented Dart Impact (73°F, Total Energy)
|
|
in·lb
|
ASTM D3763 |
|
Rockwell Hardness (R-Scale)
|
|
|
ISO 2039-2 |
|
Ball Indentation Hardness (H 358/30)
|
|
psi
|
ISO 2039-1 |
|
Heat Deflection Temperature
|
|
|
|
|
66 psi, Unannealed, 3.94 in Span 10
|
|
°F
|
ISO 75-2/Be |
|
264 psi, Unannealed, 0.126 in
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed, 3.94 in Span 10
|
|
°F
|
ISO 75-2/Ae |
|
264 psi, Unannealed, 2.52 in Span 11
|
|
°F
|
ISO 75-2/Af |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ASTM D1525 12 |
|
--
|
|
°F
|
ISO 306/A50 |
|
--
|
|
°F
|
ISO 306/B50 |
|
--
|
|
°F
|
ISO 306/B120 |
|
Ball Pressure Test (257°F)
|
|
|
IEC 60695-10-2 |
|
CLTE
|
|
|
|
|
Flow: -40 to 104°F
|
|
in/in/°F
|
ASTM E831 |
|
Flow: 73 to 176°F
|
|
in/in/°F
|
ISO 11359-2 |
|
Transverse: -40 to 104°F
|
|
in/in/°F
|
ASTM E831 |
|
Transverse: 73 to 176°F
|
|
in/in/°F
|
ISO 11359-2 |
|
Thermal Conductivity
|
|
Btu·in/hr/ft²/°F
|
ISO 8302 |
|
Surface Resistivity
|
|
ohms
|
IEC 60093 |
|
Volume Resistivity
|
|
ohm·cm
|
IEC 60093 |
|
Relative Permittivity
|
|
|
IEC 60250 |
|
50 Hz
|
|
|
|
|
60 Hz
|
|
|
|
|
1 MHz
|
|
|
|
|
Dissipation Factor
|
|
|
IEC 60250 |
|
50 Hz
|
|
|
|
|
60 Hz
|
|
|
|
|
1 MHz
|
|
|
|
|
Comparative Tracking Index
|
|
|
IEC 60112 |
|
--
|
|
V
|
|
|
Solution B
|
|
V
|
|
|
Electric Strength
|
|
|
IEC 60243-1 |
|
0.0315 in, in Oil
|
|
V/mil
|
|
|
0.0630 in, in Oil
|
|
V/mil
|
|
|
0.126 in, in Oil
|
|
V/mil
|
|
|
Flame Rating - UL
|
|
|
UL 94 |
|
0.0295 in
|
|
|
|
|
0.0984 in
|
|
|
|
|
Glow Wire Flammability Index (0.0394 in)
|
|
°F
|
IEC 60695-2-12 |
|
Oxygen Index
|
|
%
|
ISO 4589-2 |
|
RTI Str
|
|
°F
|
UL 746 |
|
RTI Imp
|
|
°F
|
UL 746 |
|
RTI Elec
|
|
°F
|
UL 746 |
|
This supplier and product may also be known by these terms: GE Plastics Europe, LNP Engineering Plastics, GE Polymerland Europe, GE Polymerland, GE Plastics
Product names can be difficult to match. You may have searched any one of these terms to find this product: VALOX* 357X Resin, VALOX 357X Resin, VALOX* , VALOX, VALOX357XResin, 357 X Resin, 357X Resin, 357X, XResin, 357XResin, Polybutylene Terephthalate, PBT, Polyester, SABIC IP Euro, PolybutyleneTerephthalate, X357
|