Density
|
|
|
|
|
--
|
|
g/cm³
|
ISO 1183 |
|
--
|
|
lb/in³
|
ISO 1183 2 |
|
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg)
|
|
in³/10min
|
ISO 1133 |
|
Molding Shrinkage - Flow
|
|
%
|
ISO 294-4 |
|
Water Absorption
|
|
|
|
|
Saturation, 73°F
|
|
%
|
ISO 62 |
|
Saturation
|
|
%
|
ISO 62 2 |
|
Viscosity number
|
|
cm³/g
|
ISO 307, 1157, 1628 2 |
|
Limiting Viscosity Number
|
|
in³/lb
|
ISO 1628-4 |
|
Tensile Modulus
|
|
psi
|
ISO 527-2 |
|
Tensile Stress (Yield)
|
|
psi
|
ISO 527-2 |
|
Tensile Strain (Yield)
|
|
%
|
ISO 527-2 |
|
Nominal Tensile Strain at Break
|
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
|
psi
|
ISO 178 |
|
Flexural Strength
|
|
psi
|
ISO 178 |
|
Notched Izod Impact Strength (73°F)
|
|
ft·lb/in²
|
ISO 180/1A |
|
Rockwell Hardness (M-Scale)
|
|
|
ISO 2039-2 |
|
Heat Deflection Temperature
|
|
|
|
|
264 psi, Unannealed
|
|
°F
|
ISO 75-2/A |
|
264 psi
|
|
°F
|
ISO 75-2 2 |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ISO 306/B50 |
|
50°C/h, B (50N)
|
|
°F
|
ISO 306 2 |
|
Ball Pressure Test (257°F)
|
|
|
IEC 60695-10-2 |
|
CLTE - Flow
|
|
in/in/°F
|
ISO 11359-2 |
|
Surface Resistivity
|
|
ohms
|
IEC 60093 |
|
Volume Resistivity
|
|
|
|
|
--
|
|
ohm·cm
|
IEC 60093 |
|
--
|
|
ohm·in
|
IEC 60093 2 |
|
Relative Permittivity
|
|
|
IEC 60250 |
|
100 Hz
|
|
|
|
|
1 MHz
|
|
|
|
|
Dissipation Factor
|
|
|
IEC 60250 |
|
100 Hz
|
|
|
|
|
1 MHz
|
|
|
|
|
Comparative Tracking Index
|
|
|
|
|
--
|
|
V
|
IEC 60112 |
|
--
|
|
|
IEC 60112 2 |
|
Electric Strength
|
|
V/mil
|
IEC 60243-1 |
|
Burning Behav. at 1.6mm nom. thickn. (0.06 in, UL)
|
|
|
ISO 1210 2 |
|
Burning Behav. at thickness h (0.118 in, UL)
|
|
|
ISO 1210 2 |
|
Flammability Classification
|
|
|
IEC 60695-11-10, -20 |
|
0.0591 in
|
|
|
|
|
0.118 in
|
|
|
|
|
Glow Wire Flammability Index
|
|
|
IEC 60695-2-12 |
|
0.0591 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
Glow Wire Ignition Temperature
|
|
|
IEC 60695-2-13 |
|
0.0591 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
Oxygen Index
|
|
%
|
ISO 4589-2 |
|
RTI Str
|
|
|
UL 746 |
|
0.0591 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
RTI Imp
|
|
|
UL 746 |
|
0.0591 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
RTI Elec
|
|
|
UL 746 |
|
0.0591 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
Comparative Tracking Index (CTI) (PLC)
|
|
|
UL 746 |
|
Transmittance
|
|
%
|
ASTM D1003 |
|
Thermal Conductivity of Melt
|
|
Btu·in/hr/ft²/°F
|
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Xantar® F 25 R, Xantar F 25 R, Xantar® , Xantar, XantarF25R, F 25 R, F25, 25R, F25R, Polycarbonate, PC, Mitsubishi EP, 25F
|
|
Features may also be described by the following terms: High Viscosity, Good Impact Resistance.
|