Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (280°C/2.16 kg)
|
|
in³/10min
|
ISO 1133 |
|
Molding Shrinkage
|
|
|
|
|
Flow: 0.0618 in
|
|
in/in
|
Internal Method |
|
Flow: 0.126 in
|
|
in/in
|
Internal Method |
|
Across Flow: 0.0618 in
|
|
in/in
|
Internal Method |
|
Across Flow: 0.126 in
|
|
in/in
|
Internal Method |
|
Across Flow 3
|
|
%
|
ISO 294-4 |
|
Flow 3
|
|
%
|
ISO 294-4 |
|
Across Flow: 0.0787 in
|
|
%
|
ISO 294-4 |
|
Flow: 0.0787 in
|
|
%
|
ISO 294-4 |
|
Water Absorption
|
|
|
|
|
Saturation, 73°F
|
|
%
|
ISO 62 |
|
Equilibrium, 73°F, 50% RH
|
|
%
|
ASTM D570 |
|
Equilibrium, 73°F, 50% RH
|
|
%
|
ISO 62 |
|
Tensile Modulus
|
|
|
|
|
-40°F
|
|
psi
|
ASTM D638 |
|
73°F
|
|
psi
|
ASTM D638 |
|
194°F
|
|
psi
|
ASTM D638 |
|
302°F
|
|
psi
|
ASTM D638 |
|
-40°F
|
|
psi
|
ISO 527-2 |
|
73°F
|
|
psi
|
ISO 527-2 |
|
Tensile Stress
|
|
|
|
|
Break, 73°F
|
|
psi
|
ISO 527-2 |
|
-40°F
|
|
psi
|
ASTM D638 |
|
73°F
|
|
psi
|
ASTM D638 |
|
194°F
|
|
psi
|
ASTM D638 |
|
302°F
|
|
psi
|
ASTM D638 |
|
Tensile Elongation
|
|
|
|
|
Break, -40°F
|
|
%
|
ASTM D638 |
|
Break, 73°F
|
|
%
|
ASTM D638 |
|
Break, 194°F
|
|
%
|
ASTM D638 |
|
Break, 302°F
|
|
%
|
ASTM D638 |
|
Break, -40°F
|
|
%
|
ISO 527-2 |
|
Break, 73°F
|
|
%
|
ISO 527-2 |
|
Tensile Creep Modulus
|
|
|
ISO 899-1 |
|
1 hr
|
|
psi
|
|
|
1000 hr
|
|
psi
|
|
|
Flexural Modulus
|
|
|
|
|
-40°F
|
|
psi
|
ASTM D790, ISO 178 |
|
73°F
|
|
psi
|
ASTM D790, ISO 178 |
|
194°F
|
|
psi
|
ASTM D790 |
|
302°F
|
|
psi
|
ASTM D790 |
|
199°F
|
|
psi
|
ISO 178 |
|
302°F
|
|
psi
|
ISO 178 |
|
Flexural Strength
|
|
|
|
|
-40°F
|
|
psi
|
ASTM D790 |
|
73°F
|
|
psi
|
ASTM D790 |
|
194°F
|
|
psi
|
ASTM D790 |
|
302°F
|
|
psi
|
ASTM D790 |
|
73°F
|
|
psi
|
ISO 178 |
|
-40°F
|
|
psi
|
ISO 178 |
|
Compressive Strength (73°F)
|
|
psi
|
ASTM D695 |
|
Shear Strength (73°F)
|
|
psi
|
ASTM D732 |
|
Charpy Notched Impact Strength
|
|
|
ISO 179/1eA |
|
-40°F
|
|
ft·lb/in²
|
|
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Charpy Unnotched Impact Strength
|
|
|
ISO 179/1eU |
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Notched Izod Impact
|
|
|
|
|
-40°F
|
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
|
ft·lb/in
|
ASTM D256 |
|
-40°F
|
|
ft·lb/in²
|
ISO 180/1A |
|
-22°F
|
|
ft·lb/in²
|
ISO 180/1A |
|
73°F
|
|
ft·lb/in²
|
ISO 180/1A |
|
Unnotched Izod Impact
|
|
|
|
|
-40°F
|
|
ft·lb/in
|
ASTM D4812 |
|
73°F
|
|
ft·lb/in
|
ASTM D4812 |
|
73°F
|
|
ft·lb/in²
|
ISO 180/1U |
|
Rockwell Hardness
|
|
|
|
|
M-Scale
|
|
|
ASTM D785 |
|
R-Scale
|
|
|
ASTM D785, ISO 2039-2 |
|
M-Scale
|
|
|
ISO 2039-2 |
|
Deflection Temperature Under Load
|
|
|
|
|
66 psi, Unannealed
|
|
°F
|
ASTM D648 |
|
66 psi, Unannealed
|
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
|
°F
|
ASTM D648, ISO 75-2/A |
|
Melting Temperature
|
|
|
|
|
-- 4
|
|
°F
|
ISO 11357-3 |
|
--
|
|
°F
|
ASTM D3418 |
|
CLTE
|
|
|
ASTM E831, ISO 11359-2 |
|
Flow: -40 to 73°F
|
|
in/in/°F
|
|
|
Flow: 73 to 131°F
|
|
in/in/°F
|
|
|
Flow: 131 to 320°F
|
|
in/in/°F
|
|
|
Flow: 73 to 131°F, 0.0787 in
|
|
in/in/°F
|
|
|
Transverse: -40 to 73°F
|
|
in/in/°F
|
|
|
Transverse: 73 to 131°F
|
|
in/in/°F
|
|
|
Transverse: 131 to 320°F
|
|
in/in/°F
|
|
|
Transverse: 73 to 131°F, 0.0787 in
|
|
in/in/°F
|
|
|
Surface Resistivity
|
|
ohms
|
ASTM D257, IEC 60093 |
|
Volume Resistivity
|
|
|
|
|
73°F
|
|
ohm·cm
|
ASTM D257 |
|
--
|
|
ohm·cm
|
IEC 60093 |
|
Dielectric Strength
|
|
|
|
|
73°F, 0.0630 in, in Oil 5
|
|
V/mil
|
ASTM D149 |
|
73°F, 0.126 in, in Oil 5
|
|
V/mil
|
ASTM D149 |
|
203°F, 0.0630 in, in Oil 5
|
|
V/mil
|
ASTM D149 |
|
203°F, 0.126 in, in Oil 5
|
|
V/mil
|
ASTM D149 |
|
302°F, 0.0630 in, in Oil 5
|
|
V/mil
|
ASTM D149 |
|
302°F, 0.126 in, in Oil 5
|
|
V/mil
|
ASTM D149 |
|
73°F, 0.0394 in
|
|
V/mil
|
IEC 60243-1 |
|
Dielectric Constant
|
|
|
|
|
73°F, 1 kHz
|
|
|
ASTM D150 |
|
73°F, 1 MHz
|
|
|
ASTM D150 |
|
73°F, 100 Hz
|
|
|
IEC 60250 |
|
73°F, 1 MHz
|
|
|
IEC 60250 |
|
Dissipation Factor
|
|
|
|
|
73°F, 1 kHz
|
|
|
ASTM D150 |
|
73°F, 1 MHz
|
|
|
ASTM D150 |
|
73°F, 100 Hz
|
|
|
IEC 60250 |
|
73°F, 1 MHz
|
|
|
IEC 60250 |
|
Comparative Tracking Index
|
|
V
|
IEC 60112 |
|
Flame Rating - UL
|
|
|
UL 94 |
|
0.0319 in
|
|
|
|
|
0.0591 in
|
|
|
|
|
0.0787 in
|
|
|
|
|
0.118 in
|
|
|
|
|
0.236 in
|
|
|
|
|
Flammability Classification
|
|
|
IEC 60695-11-10, -20 |
|
0.0319 in
|
|
|
|
|
0.0591 in
|
|
|
|
|
0.0787 in
|
|
|
|
|
0.118 in
|
|
|
|
|
0.236 in
|
|
|
|
|
Glow Wire Flammability Index
|
|
|
IEC 60695-2-12 |
|
0.0787 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
Oxygen Index
|
|
%
|
ASTM D2863, ISO 4589-2 |
|
RTI Str
|
|
|
UL 746 |
|
0.0319 in
|
|
°F
|
|
|
0.0591 in
|
|
°F
|
|
|
0.0787 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
0.236 in
|
|
°F
|
|
|
RTI Imp
|
|
|
UL 746 |
|
0.0319 in
|
|
°F
|
|
|
0.0591 in
|
|
°F
|
|
|
0.0787 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
0.236 in
|
|
°F
|
|
|
RTI Elec
|
|
|
UL 746 |
|
0.0319 in
|
|
°F
|
|
|
0.0591 in
|
|
°F
|
|
|
0.0787 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
0.236 in
|
|
°F
|
|
|
Comparative Tracking Index (CTI)
|
|
V
|
UL 746 |
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Rynite® 530 NC010, Rynite 530 NC010, Rynite® , Rynite, Rynite530NC010, 530 NC 010, 530 NC010, 530NC, NC010, 530NC010, Polyethylene Terephthalate, PET, Polyester, DuPont, PolyethyleneTerephthalate, NC530
|
|
Features may also be described by the following terms: Heat Stabilized, Heat-ageing Stabilized, Heat Ageing Stabilized, Heat-aging Stabilized, Heat Aging Stabilized, Good Electrical Properties, Good Stiffness, Good Strength, Good Thermal Aging Resistance, Thermal Aging Resistant, Ultrasonic Weldable.
|
|
Uses may also be described by the following terms: Housings, Housing, Electrical Applications, Electronic Applications, Electrical/Electronic Applications, Electrical Sector, Automotive Applications, Automotive Sector.
|
|
This plastic material has approval for 3 automotive specifications from the following agencies (the number in parentheses shows the number of specifications for that agency): ASTM (1), FORD (1), GM (1).
|