Fortron® 1130L4 Ticona Polyphenylene Sulfide (Glass Fiber Reinforcement, 30%)

Product Description

Fortron 1130L4 is a 30% glass-reinforced PPS that has excellent heat and chemical resistance. It is inherently flame-retardant and exhibits high hardness and a good balance of strength and stiffness. Especially used for thin walled parts requiring long flow lengths. This grade also exhibits excellent weldability in secondary operations due to its low filler content.

General

Material Status

Commercial: Active

Availability

Africa & Middle East

Europe

Latin America

North America

South America

Filler / Reinforcement

Glass Fiber Reinforcement, 30% Filler by Weight

Features

Flame Retardant

Good Chemical Resistance

Good Stiffness

Good Strength

Halogen Free

High Hardness

High Heat Resistance

Weldable

Uses

Thin-walled Parts

RoHS Compliance

Processing Method

Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity
--			ASTM D792
--		g/cm³	ISO 1183
Specific Volume		in³/lb	ASTM D792
Molding Shrinkage
Flow: 0.125 in		in/in	ASTM D955
Across Flow: 0.125 in		in/in	ASTM D955
Across Flow		%	ISO 294-4
Flow		%	ISO 294-4
Water Absorption
73°F, 24 hr		%	ASTM D570
Saturation, 73°F		%	ISO 62
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus		psi	ISO 527-2/1A/1
Tensile Strength
Break, 73°F		psi	ASTM D638
Break		psi	ISO 527-2/1A/5
Tensile Elongation
Break, 73°F		%	ASTM D638
Break		%	ISO 527-2/1A/5
Flexural Modulus (73°F)		psi	ASTM D790, ISO 178
Flexural Strength
73°F		psi	ASTM D790
--²		psi	ISO 178
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1 e A
-22°F		ft·lb/in²
73°F		ft·lb/in²
Charpy Unnotched Impact Strength			ISO 179/1 eU
-22°F		ft·lb/in²
73°F		ft·lb/in²
Notched Izod Impact
73°F		ft·lb/in	ASTM D256
-22°F		ft·lb/in²	ISO 180/1A
73°F		ft·lb/in²	ISO 180/1A
Unnotched Izod Impact
73°F		ft·lb/in	ASTM D256
73°F		ft·lb/in²	ISO 180/1U
Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)			ASTM D785, ISO 2039-2
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
66 psi, Unannealed		°F	ASTM D648
264 psi, Unannealed		°F	ASTM D648
264 psi, Unannealed		°F	ISO 75-2/A
Glass Transition Temperature		°F	ISO 11357-2
CLTE			ISO 11359-2
Flow		in/in/°F
Transverse		in/in/°F
Electrical	Nominal Value	Unit	Test Method
Surface Resistivity		ohm	IEC 60093
Volume Resistivity
--		ohm·cm	ASTM D257
--		ohm·cm	IEC 60093
Dissipation Factor			ASTM D150
1 kHz
1 MHz
Arc Resistance		sec	ASTM D495
Comparative Tracking Index		V	ASTM D3638
Flammability	Nominal Value	Unit	Test Method
Flame Rating - UL			UL 94
0.0315 in
0.0591 in
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Fortron® 1130L4, Fortron 1130L4, Fortron® , Fortron, Fortron1130L4, 1130 L 4, 1130L4, 1130L, L4, Polyphenylene Sulfide, PPS, Ticona, PolyphenyleneSulfide, L1130
Features
Features may also be described by the following terms: High Hardness, Hard, High Heat Resistance, Good Stiffness, Good Strength, Good Chemical Resistance, Chemical Resistant, Zero Halogen Content, Halogen Free.
Uses
Uses may also be described by the following terms: Thin-walled Parts, Thin Walled Parts, Thin-wall Parts, Thin wall Parts, Thinwall Parts.

Injection	Nominal Value	Unit
Processing (Melt) Temp		°F
Mold Temperature		°F
Injection Notes
On injection molding machines with 15-25 D long three-section screws, as are usual in the trade, the FORTRON is processable. A shut-off nozzle is preferred to a free-flow nozzle. A medium injection rate is normally preferred. All mold cavities must be effectively vented.

Notes

¹Typical properties: these are not to be construed as specifications.

²at Break

Fortron® 1130L4

Polyphenylene Sulfide

Glass Fiber Reinforcement, 30%

Supplied by Ticona