°F
|
ISO 306/B50, ISO 306/B120 |
|
Impact Flexural Test, ISO 179/2C, Notched: 17 kJ/m²
Impact Flexural Test, ISO 179/2D, Unnotched: No Break
Vicat Softening Temp, DIN 53460, 50°C/hr ; 1 kg: 104°C
Vicat Softening Temp, DIN 53460, 50°C/hr ; 5 kg: 98°C
Vicat Softening Temp, DIN 53460, 120°C/hr ; 1 kg: 106°C
Vicat Softening Temp, DIN 53460, 120°C/hr ; 5 kg: 98°C
DTUL @ 1.80 MPa, DIN 53461, Unannealed: 80°C
DTUL @ 1.80 MPa, DIN 53461, Annealed: 99°C
Impact Flexural Test, DIN 53453, Notched: 17 kJ/m²
Impact Flexural Test, DIN 53453, Unnotched: No Break
Tensile Strength @ Yield, DIN 53455, 50 mm/min: 47 MPa
Tensile Strength @ Break, DIN 53455, 50 mm/min: 35 MPa
Tensile Elongation, DIN 53455, 50 mm/min: 15%
Flexural Strength, DIN 53452, 2 mm/min: 65 MPa
Flexural Modulus, DIN 53452, 2 mm/min: 2.0 GPa
Mass Density, DIN 53479-A, 23°C: 1.03 g/cm³
|
|
This supplier and product may also be known by these terms: ChiMei
Product names can be difficult to match. You may have searched any one of these terms to find this product: POLYLAC® PA-746Y, POLYLAC PA746Y, POLYLAC® , POLYLAC, POLYLACPA746Y, PA, PA 746 Y, PA-746Y, PA746Y, PA:746Y, PA/746Y, PA+746Y, PA_746Y, PA 746Y, PA746, 746Y, Acrylonitrile Butadiene Styrene, ABS, Chi Mei, AcrylonitrileButadieneStyrene, 746PA
|
|
Features may also be described by the following terms: Good Chemical Resistance, Chemical Resistant, High Impact Resistance, Medium Flow, Medium Melt, Medium MFI.
|