Amilan CM1011G-30 Toray Polyamide 6 (Glass Fiber Reinforcement, 30%)

General

Material Status

Commercial: Active

Availability

Asia Pacific

Europe

North America

Filler / Reinforcement

Glass Fiber Reinforcement, 30% Filler by Weight

Forms

Pellets

Processing Method

Injection Molding

Physical	Dry	Conditioned	Unit	Test Method
Density		--	g/cm³	ISO 1183
Molding Shrinkage				ISO 294-4
Across Flow: 0.118 in		--	%
Flow: 0.118 in		--	%
Water Absorption				ISO 62
73°F, 24 hr		--	%
Saturation, 73°F		--	%
Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Stress				ISO 527-2
Yield, -40°F			psi
Yield, 73°F			psi
Yield, 176°F			psi
Tensile Strain				ISO 527-2
Break, -40°F			%
Break, 73°F			%
Break, 176°F			%
Flexural Modulus				ISO 178
-40°F			psi
73°F			psi
176°F			psi
Flexural Strength				ISO 178
176°F			psi
73°F			psi
-40°F			psi
Compressive Stress				ISO 604
-40°F			psi
73°F			psi
176°F			psi
Shear Strength (73°F)		--	psi	ASTM D732
Taber Abrasion Resistance (1000 Cycles)		--	mg	ASTM D1044
Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179
-40°F			ft·lb/in²
73°F			ft·lb/in²
Charpy Unnotched Impact Strength				ISO 179
-40°F			ft·lb/in²
73°F			ft·lb/in²
Hardness	Dry	Conditioned	Unit	Test Method
Rockwell Hardness				ISO 2039-2
M-Scale, 73°F		--
R-Scale, 73°F		--
Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
66 psi, Unannealed		--	°F	ISO 75-2/B
264 psi, Unannealed		--	°F	ISO 75-2/A
Melting Temperature (DSC)		--	°F	ISO 3146
CLTE - Flow		--	in/in/°F	ISO 11359-2
Electrical	Dry	Conditioned	Unit	Test Method
Volume Resistivity			ohm·cm	IEC 60093
Dielectric Constant				IEC 60250
50 Hz
1 kHz
1 MHz
Dissipation Factor				IEC 60250
73°F, 50 Hz
73°F, 1 kHz
73°F, 1 MHz
Electric Strength			V/mil	IEC 60243-1
Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating - UL				UL 94
0.0625 in		--
0.0626 in	--
Additional Information
Dry	Arc Resistance, UL746A, Tungsten Electrode: 131 sec Coefficient of Friction, vs metal with lubrication, Suzuki method: <0.15 Coefficient of Friction, vs metal without lubrication, Suzuki method: 0.35 Specific Heat: 1.6 J/g/°C Thermal Conductivity: 0.38 W/m/°C
Conditioned	Arc Resistance, UL746A, Tungsten Electrode: 137 sec
Related Terminology
Dry	Product names can be difficult to match. You may have searched any one of these terms to find this product: Amilan® CM1011G-30, Amilan CM1011G30, Amilan® , Amilan, AmilanCM1011G30, CM 1011 G, CM1011G, CM 1011 G 30, CM1011G-30, CM1011G30, CM1011G:30, CM1011G/30, CM1011G+30, CM1011G_30, CM1011G 30, CM1011, 1011G, G30, Polyamide 6, Nylon 6, Polyamide, Nylon, pa6, Toray, Polyamide6, Nylon6, 1011CM
Generic Name
Dry	Generic Name may also be described by the following terms: PA6.
Conditioned	Product names can be difficult to match. You may have searched any one of these terms to find this product: Amilan® CM1011G-30, Amilan CM1011G30, Amilan® , Amilan, AmilanCM1011G30, CM 1011 G, CM1011G, CM 1011 G 30, CM1011G-30, CM1011G30, CM1011G:30, CM1011G/30, CM1011G+30, CM1011G_30, CM1011G 30, CM1011, 1011G, G30, Polyamide 6, Nylon 6, Polyamide, Nylon, pa6, Toray, Polyamide6, Nylon6, 1011CM Generic Name may also be described by the following terms: PA6.

Notes

¹Typical properties: these are not to be construed as specifications.

Amilan® CM1011G-30

Polyamide 6

Glass Fiber Reinforcement, 30%

Supplied by Toray Resin Company