Specific Gravity
|
|
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR) (280°C/2.16 kg)
|
|
g/10 min
|
ASTM D1238 |
|
Molding Shrinkage - Flow
|
|
in/in
|
ASTM D955 |
|
Water Absorption (Equilibrium, 73°F, 50% RH)
|
|
%
|
ASTM D570 |
|
Tensile Modulus
|
|
psi
|
ASTM D638 |
|
Tensile Strength
|
|
psi
|
ASTM D638 |
|
Tensile Elongation (Break)
|
|
%
|
ASTM D638 |
|
Flexural Modulus
|
|
psi
|
ASTM D790 |
|
Flexural Strength
|
|
psi
|
ASTM D790 |
|
Water Vapor Transmission
|
|
g/100 in²/24 hr
|
ASTM E96 |
|
Notched Izod Impact
|
|
ft·lb/in
|
ASTM D256 |
|
Rockwell Hardness (R-Scale)
|
|
|
ASTM D785 |
|
Deflection Temperature Under Load (264 psi, Unannealed)
|
|
°F
|
ASTM D648 |
|
Glass Transition Temperature (DSC)
|
|
°F
|
DSC |
|
Vicat Softening Temperature
|
|
°F
|
ASTM D1525 |
|
CLTE - Flow
|
|
in/in/°F
|
ASTM D696 |
|
Volume Resistivity
|
|
ohm·cm
|
ASTM D257 |
|
Dielectric Strength
|
|
V/mil
|
ASTM D149 |
|
Dielectric Constant (1 MHz)
|
|
|
ASTM D150 |
|
Dissipation Factor (1 MHz)
|
|
|
ASTM D150 |
|
Refractive Index
|
|
|
ASTM D542 |
|
Transmittance
|
|
%
|
ASTM D1003 |
|
The value listed as Water Vapor Transmittance, ASTM E96, was tested in accordance with JIS Z 0208.
The value listed as Melt Flow Rate, ASTM D1238, was tested in accordance with JIS K 6719.
Volume Resistively, ASTM D257: >10^16 ohm cm
Dielectric Breakdown Strength, ASTM D149: >70 KV/mm
Water Absorption, ASTM D570, 50%RH @ 22.7°C: <.01 %
Thermal Decomposition Temperature: 420°C
Moisture permeability 24hrs, JIS Z 2080, 90% RH 40°C .15mm: .67
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Zeonor 1420R, Zeonor , Zeonor1420R, 1420 R, 1420R, Polyolefin, Unspecified, Polyolefin Unspecified, Polyolefin, Nippon Zeon, PolyolefinUnspecified, R1420
|
|
Features may also be described by the following terms: High Clarity, Low Water Absorption, Low Moisture Absorption, Water Resistant, Moisure Resistant, Good Thermal Stability, High Flow, High Melt, High MFI.
|
|
Uses may also be described by the following terms: Electrical Applications, Electronic Applications, Electrical/Electronic Applications, Electrical Sector, Automotive Applications, Automotive Sector.
|