| Specific Gravity |
|
|
ASTM D792 |
| Melt Mass-Flow Rate (MFR) (280°C/2.16 kg) |
|
g/10 min
|
ASTM D1238 |
| Molding Shrinkage - Flow |
|
in/in
|
ASTM D955 |
| Water Absorption (Equilibrium, 73°F, 50% RH) |
|
%
|
ASTM D570 |
| Tensile Modulus |
|
psi
|
ASTM D638 |
| Tensile Strength |
|
psi
|
ASTM D638 |
| Tensile Elongation (Break) |
|
%
|
ASTM D638 |
| Flexural Modulus |
|
psi
|
ASTM D790 |
| Flexural Strength |
|
psi
|
ASTM D790 |
| Water Vapor Transmission |
|
g/100 in²/24 hr
|
ASTM E96 |
| Notched Izod Impact |
|
ft·lb/in
|
ASTM D256 |
| Rockwell Hardness (R-Scale) |
|
|
ASTM D785 |
| Deflection Temperature Under Load (264 psi, Unannealed) |
|
°F
|
ASTM D648 |
| Glass Transition Temperature (DSC) |
|
°F
|
DSC |
| Vicat Softening Temperature |
|
°F
|
ASTM D1525 |
| CLTE - Flow |
|
in/in/°F
|
ASTM D696 |
| Volume Resistivity |
|
ohm·cm
|
ASTM D257 |
| Dielectric Strength |
|
V/mil
|
ASTM D149 |
| Dielectric Constant (1 MHz) |
|
|
ASTM D150 |
| Dissipation Factor (1 MHz) |
|
|
ASTM D150 |
| Refractive Index |
|
|
ASTM D542 |
| Transmittance |
|
%
|
ASTM D1003 |
|
The value listed as Water Vapor Transmittance, ASTM E96, was tested in accordance with JIS Z 0208.
The value listed as Melt Flow Rate, ASTM D1238, was tested in accordance with JIS K 6719.
Volume Resistively, ASTM D257: >10^16 ohm cm
Dielectric Breakdown Strength, ASTM D149: >70 KV/mm
Water Absorption, ASTM D570, 50%RH @ 22.7°C: <.01 %
Thermal Decomposition Temperature: 420°C
Moisture permeability 24hrs, JIS Z 2080, 90% RH 40°C .08 mm: 1.58
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Zeonor 1600R, Zeonor , Zeonor1600R, 1600 R, 1600R, Polyolefin, Unspecified, Polyolefin Unspecified, Polyolefin, Nippon Zeon, PolyolefinUnspecified, R1600
|
|
Features may also be described by the following terms: High Clarity, Low Water Absorption, Low Moisture Absorption, Water Resistant, Moisure Resistant, Good Thermal Stability, High Flow, High Melt, High MFI.
|
|
Uses may also be described by the following terms: Electrical Applications, Electronic Applications, Electrical/Electronic Applications, Electrical Sector, Automotive Applications, Automotive Sector.
|