Density
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)
|
|
g/10 min
|
ISO 1133 |
|
Tensile Stress
|
|
|
ISO 527-2 |
|
Yield, 73°F
|
|
psi
|
|
|
Break, 73°F
|
|
psi
|
|
|
Tensile Strain
|
|
|
ISO 527-2 |
|
Yield, 73°F
|
|
%
|
|
|
Break, 73°F
|
|
%
|
|
|
Flexural Modulus (73°F)
|
|
psi
|
ISO 178 |
|
Film Thickness - Tested
|
|
mil
|
|
|
Secant Modulus
|
|
|
ASTM D882 |
|
MD: 2.0 mil, Blown Film
|
|
psi
|
|
|
TD: 2.0 mil, Blown Film
|
|
psi
|
|
|
Tensile Strength
|
|
|
ASTM D882 |
|
MD: Yield, 2.0 mil, Blown Film
|
|
psi
|
|
|
TD: Yield, 2.0 mil, Blown Film
|
|
psi
|
|
|
MD: Break, 2.0 mil, Blown Film
|
|
psi
|
|
|
TD: Break, 2.0 mil, Blown Film
|
|
psi
|
|
|
Tensile Elongation
|
|
|
ASTM D882 |
|
MD: Break, 2.0 mil, Blown Film
|
|
%
|
|
|
TD: Break, 2.0 mil, Blown Film
|
|
%
|
|
|
Dart Drop Impact (2.0 mil, Blown Film)
|
|
g
|
ISO 7765-1 |
|
Elmendorf Tear Strength
|
|
|
ISO 6383-2 |
|
MD: 2.0 mil, Blown Film
|
|
lbf
|
|
|
TD: 2.0 mil, Blown Film
|
|
lbf
|
|
|
Durometer Hardness (Shore D)
|
|
|
ASTM D2240, ISO 868 |
|
Heat Deflection Temperature (66 psi, Unannealed)
|
|
°F
|
ISO 75-2/B |
|
Vicat Softening Temperature
|
|
°F
|
ISO 306/A50 |
|
Melting Temperature
|
|
°F
|
DSC |
|
Heat Resistance
|
|
°F
|
Internal Method |
|
This supplier and product may also be known by these terms: LyondellBasell Industries, Lyondell, Basell, Bassell, Basell Polyolefins, Bassel
Product names can be difficult to match. You may have searched any one of these terms to find this product: Adflex Q 401 F, Adflex , AdflexQ401F, Q 401 F, Q401, 401F, Q401F, Polyolefin, Unspecified, Polyolefin Unspecified, Polyolefin, LyondellBasell, PolyolefinUnspecified, 401Q
|
|
Features may also be described by the following terms: High Heat Resistance, Good Puncture Resistance, Puncture Resistant, Good Tear Strength, Slip, Unspecified Slip, Antiblocking, Unspecified Antiblock.
|