| Specific Gravity |
|
|
ASTM D792 |
|
--
|
|
|
|
|
--
|
|
g/cm³
|
|
| Specific Volume |
|
in³/lb
|
ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) |
|
g/10 min
|
ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) |
|
in³/10min
|
ISO 1133 |
| Molding Shrinkage - Flow (0.126 in) |
|
in/in
|
Internal Method |
| Water Absorption |
|
|
ASTM D570 |
|
24 hr
|
|
%
|
|
|
Equilibrium, 73°F
|
|
%
|
|
|
Equilibrium, 212°F
|
|
%
|
|
| Tensile Modulus |
|
|
|
|
-- 2
|
|
psi
|
ASTM D638 |
|
--
|
|
psi
|
ISO 527-2/1 |
| Tensile Strength |
|
|
|
|
Yield 3
|
|
psi
|
ASTM D638 |
|
Yield
|
|
psi
|
ISO 527-2/50 |
|
Break 3
|
|
psi
|
ASTM D638 |
|
Break
|
|
psi
|
ISO 527-2/50 |
| Tensile Elongation |
|
|
|
|
Yield 3
|
|
%
|
ASTM D638 |
|
Yield
|
|
%
|
ISO 527-2/50 |
|
Break 3
|
|
%
|
ASTM D638 |
|
Break
|
|
%
|
ISO 527-2/50 |
| Flexural Modulus |
|
|
|
|
1.97 in Span 4
|
|
psi
|
ASTM D790 |
|
-- 5
|
|
psi
|
ISO 178 |
| Flexural Strength |
|
|
|
|
-- 5, 6
|
|
psi
|
ISO 178 |
|
Yield, 1.97 in Span 4
|
|
psi
|
ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) |
|
mg
|
ASTM D1044 |
| Charpy Notched Impact Strength 7 |
|
|
ISO 179/1eA |
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
| Notched Izod Impact |
|
|
|
|
Natural, Tints
|
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
|
ft·lb/in
|
ASTM D256 |
|
-22°F 8
|
|
ft·lb/in²
|
ISO 180/1A |
|
73°F 8
|
|
ft·lb/in²
|
ISO 180/1A |
| Unnotched Izod Impact (73°F) |
|
ft·lb/in
|
ASTM D4812 |
| Instrumented Dart Impact (73°F, Energy at Peak Load) |
|
in·lb
|
ASTM D3763 |
| Gardner Impact (73°F) |
|
in·lb
|
ASTM D3029 |
| Tensile Impact Strength 9 |
|
ft·lb/in²
|
ASTM D1822 |
| Rockwell Hardness |
|
|
ASTM D785 |
|
M-Scale
|
|
|
|
|
R-Scale
|
|
|
|
| Deflection Temperature Under Load |
|
|
|
|
66 psi, Unannealed, 0.252 in
|
|
°F
|
ASTM D648 |
|
66 psi, Unannealed, 3.94 in Span 10
|
|
°F
|
ISO 75-2/Be |
|
264 psi, Unannealed, 0.126 in
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed, 0.252 in
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed, 3.94 in Span 10
|
|
°F
|
ISO 75-2/Ae |
| Vicat Softening Temperature |
|
|
|
|
--
|
|
°F
|
ISO 306/B50 |
|
--
|
|
°F
|
ISO 306/B120 |
| Ball Pressure Test (257°F) |
|
|
IEC 60695-10-2 |
| CLTE - Flow |
|
|
|
|
-40 to 203°F
|
|
in/in/°F
|
ASTM E831 |
|
73 to 176°F
|
|
in/in/°F
|
ISO 11359-2 |
| Specific Heat |
|
Btu/lb/°F
|
ASTM C351 |
| Thermal Conductivity |
|
|
|
|
--
|
|
Btu·in/hr/ft²/°F
|
ASTM C177 |
|
--
|
|
Btu·in/hr/ft²/°F
|
ISO 8302 |
| Surface Resistivity |
|
ohms
|
IEC 60093 |
| Volume Resistivity |
|
|
|
|
--
|
|
ohm·cm
|
ASTM D257 |
|
--
|
|
ohm·cm
|
IEC 60093 |
| Dielectric Strength |
|
|
|
|
0.126 in, in Air
|
|
V/mil
|
ASTM D149 |
|
0.126 in, in Oil
|
|
V/mil
|
IEC 60243-1 |
| Dielectric Constant |
|
|
|
|
50 Hz
|
|
|
ASTM D150 |
|
60 Hz
|
|
|
ASTM D150 |
|
1 MHz
|
|
|
ASTM D150 |
|
50 Hz
|
|
|
IEC 60250 |
|
60 Hz
|
|
|
IEC 60250 |
|
1 MHz
|
|
|
IEC 60250 |
| Dissipation Factor |
|
|
|
|
50 Hz
|
|
|
ASTM D150 |
|
60 Hz
|
|
|
ASTM D150 |
|
1 MHz
|
|
|
ASTM D150, IEC 60250 |
|
50 Hz
|
|
|
IEC 60250 |
|
60 Hz
|
|
|
IEC 60250 |
| Flame Rating - UL (0.0429 in) |
|
|
UL 94 |
| Oxygen Index |
|
%
|
ISO 4589-2 |
| RTI Str |
|
°F
|
UL 746 |
| RTI Imp |
|
°F
|
UL 746 |
| RTI Elec |
|
°F
|
UL 746 |
| Comparative Tracking Index (CTI) (PLC) |
|
|
UL 746 |
| High Voltage Arc Tracking Rate (HVTR) (PLC) |
|
|
UL 746 |
| Hot-wire Ignition (HWI) (PLC) |
|
|
UL 746 |
| High Amp Arc Ignition (HAI) (PLC) |
|
|
UL 746 |
| Refractive Index |
|
|
ASTM D542 |
| Transmittance (100 mil) |
|
%
|
ASTM D1003 |
| Haze (100 mil) |
|
%
|
ASTM D1003 |
|
This supplier and product may also be known by these terms: GE Plastics, LNP Engineering Plastics, GE Polymerland
Product names can be difficult to match. You may have searched any one of these terms to find this product: LEXAN* HP1 Resin, LEXAN HP1 Resin, LEXAN* , LEXAN, LEXANHP1Resin, HP 1 Resin, HP1 Resin, HP1, 1Resin, HP1Resin, Polycarbonate, PC, SABIC IP, 1HP
|
|
Features may also be described by the following terms: Ethylene Oxide Sterilizable, EtO Sterilizable, EtO Sterilization, Ethylene Oxide Sterilizable, High Flow, High Melt, High MFI.
|
|
Uses may also be described by the following terms: Medical Applications.
|
|
This plastic material has 2 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): USP (1), ISO (1).
|