XENOY* 6370 Resin

Polycarbonate + PBT

Glass Fiber Reinforcement, 30%

Supplied by SABIC Innovative Plastics

The technical datasheet with complete property values for XENOY* 6370 Resin is available to members of the Prospector Plastics Database.
Register to view full datasheet.
Register to View Full Datasheet
Product Description
30% glass-reinforced, impact modified thermoplastic alloy. Improved toughness and ductility.
General  
Material Status 
  • Commercial: Active
Availability 
  • North America
Filler / Reinforcement 
  • Glass Fiber Reinforcement, 30% Filler by Weight
Additive 
  • Impact Modifier
Features 
  • Ductile
  • Good Toughness
  • Impact Modified
Processing Method 
  • Injection Molding
Multi-Point Data 
  • Coefficient of Thermal Expansion vs. Temperature (ASTM E831)
  • Elastic Modulus vs Temperature (ASTM D4065)
  • Flexural DMA (ASTM D4065)
  • Instrumented Impact (Energy) (ASTM D3763)
  • Instrumented Impact (Load) (ASTM D3763)
  • Shear DMA (ASTM D4065)
  • Tensile Creep (ASTM D2990)
  • Tensile Fatigue
  • Tensile Stress vs. Strain (ASTM D638)
  • Thermal Conductivity vs. Temperature (ASTM E1530)
Physical
Nominal Value
Unit
Test Method
Specific Gravity
      
--
 
 ASTM D792
--
g/cm³
 ISO 1183
Specific Volume
in³/lb
 ASTM D792
Melt Mass-Flow Rate (MFR) (250°C/5.0 kg)
g/10 min
 ASTM D1238
Melt Volume-Flow Rate (MVR)
     ISO 1133
250°C/5.0 kg
in³/10min
  
265°C/5.0 kg
in³/10min
  
Molding Shrinkage
     Internal Method
Flow  2
in/in
  
Flow  3
in/in
  
Across Flow  2
in/in
  
Across Flow  3
in/in
  
Water Absorption
      
24 hr
%
 ASTM D570
Saturation, 73°F
%
 ISO 62
Equilibrium, 73°F, 50% RH
%
 ISO 62
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
      
-- 4
psi
 ASTM D638
--
psi
 ISO 527-2/1
Tensile Strength
      
Yield 5
psi
 ASTM D638
Yield
psi
 ISO 527-2/5
Break 5
psi
 ASTM D638
Break
psi
 ISO 527-2/5
Tensile Elongation
      
Yield 5
%
 ASTM D638
Yield
%
 ISO 527-2/5
Break 5
%
 ASTM D638
Break
%
 ISO 527-2/5
Flexural Modulus
      
1.97 in Span 6
psi
 ASTM D790
-- 7
psi
 ISO 178
Flexural Strength
      
-- 7, 8
psi
 ISO 178
Yield, 1.97 in Span 6
psi
 ASTM D790
Break, 1.97 in Span 6
psi
 ASTM D790
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength 9 (73°F)
ft·lb/in²
 ISO 179/1eA
Notched Izod Impact
      
-22°F
ft·lb/in
 ASTM D256
73°F
ft·lb/in
 ASTM D256
-22°F 10
ft·lb/in²
 ISO 180/1A
73°F 10
ft·lb/in²
 ISO 180/1A
Unnotched Izod Impact (73°F)
ft·lb/in
 ASTM D4812
Instrumented Dart Impact
     ASTM D3763
73°F, Energy at Peak Load
in·lb
  
73°F, Total Energy
in·lb
  
Hardness
Nominal Value
Unit
Test Method
Rockwell Hardness (R-Scale)
 
 ASTM D785
Thermal
Nominal Value
Unit
Test Method
Deflection Temperature Under Load
      
66 psi, Unannealed, 0.252 in
°F
 ASTM D648
264 psi, Unannealed, 0.126 in
°F
 ASTM D648
264 psi, Unannealed, 0.252 in
°F
 ASTM D648
264 psi, Unannealed, 2.52 in Span 11
°F
 ISO 75-2/Af
Vicat Softening Temperature
      
--
°F
 ASTM D1525 12
--
°F
 ISO 306/B50
--
°F
 ISO 306/B120
CLTE
      
Flow: -40 to 104°F
in/in/°F
 ASTM E831, ISO 11359-2
Flow: 140 to 280°F
in/in/°F
 ASTM E831
Transverse: -40 to 104°F
in/in/°F
 ASTM E831, ISO 11359-2
Electrical
Nominal Value
Unit
Test Method
Volume Resistivity
ohm·cm
 ASTM D257
Dielectric Strength
     ASTM D149
0.0630 in, in Oil
V/mil
  
0.126 in, in Air
V/mil
  
Dielectric Constant
     ASTM D150
100 Hz
 
  
1 MHz
 
  
Dissipation Factor
     ASTM D150
100 Hz
 
  
1 MHz
 
  
Arc Resistance (PLC) 13
 
 ASTM D495
Flammability
Nominal Value
Unit
Test Method
Flame Rating - UL (0.0591 in)
 
 UL 94
UL
Nominal Value
Unit
Test Method
RTI Str
°F
 UL 746
RTI Imp
°F
 UL 746
RTI Elec
°F
 UL 746
Comparative Tracking Index (CTI) (PLC)
 
 UL 746
High Voltage Arc Tracking Rate (HVTR) (PLC)
 
 UL 746
Hot-wire Ignition (HWI) (PLC)
 
 UL 746
High Amp Arc Ignition (HAI) (PLC)
 
 UL 746
Related Terminology
This supplier and product may also be known by these terms: GE Plastics, LNP Engineering Plastics, GE Polymerland

Product names can be difficult to match. You may have searched any one of these terms to find this product: XENOY* 6370 Resin, XENOY 6370 Resin, XENOY* , XENOY, XENOY6370Resin, 6370 Resin, 6370Resin, Polycarbonate + PBT, Polycarbonate PBT, Polycarbonate : PBT, Polycarbonate / PBT, Polycarbonate - PBT, Polycarbonate _ PBT, Polycarbonate PBT, PC+PBT, PCPBT, PC:PBT, PC/PBT, PC-PBT, PC_PBT, PC PBT, Polycarbonate, PC, SABIC IP, PolycarbonatePBT, Polycarbonate_PBT, Resin6370
Features
Features may also be described by the following terms: Good Toughness, Tough.
Injection
Nominal Value
Unit
 
Drying Temperature
°F
  
Drying Time
hr
  
Drying Time, Maximum
hr
  
Suggested Max Moisture
%
  
Suggested Shot Size
%
  
Rear Temperature
°F
  
Middle Temperature
°F
  
Front Temperature
°F
  
Nozzle Temperature
°F
  
Processing (Melt) Temp
°F
  
Mold Temperature
°F
  
Back Pressure
psi
  
Screw Speed
rpm
  
Vent Depth
in
  
Notes
1Typical properties: these are not to be construed as specifications.
20.75 to 2.3 mm
32.3 to 4.6 mm
40.20 in/min
5Type I, 0.20 in/min
60.051 in/min
70.079 in/min
8Yield
980*10*4 sp=62mm
1080*10*4
1180*10*4 mm
12Rate B (120°C/h), Loading 2 (50 N)
13Tungsten Electrode
 
IDES
Copyright © 2012 IDES
The information presented on this datasheet was acquired by IDES from the producer of the material. IDES makes substantial efforts to assure the accuracy of this data. However, IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.