| Specific Gravity |
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
| Specific Volume |
|
in³/lb
|
ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) |
|
g/10 min
|
ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) |
|
in³/10min
|
ISO 1133 |
| Molding Shrinkage |
|
|
Internal Method |
|
Flow 2
|
|
in/in
|
|
|
Flow 3
|
|
in/in
|
|
|
Flow: 0.126 in
|
|
in/in
|
|
|
Across Flow 2
|
|
in/in
|
|
|
Across Flow 3
|
|
in/in
|
|
| Water Absorption |
|
|
|
|
24 hr
|
|
%
|
ASTM D570 |
|
Saturation, 73°F
|
|
%
|
ISO 62 |
|
Equilibrium, 73°F, 50% RH
|
|
%
|
ISO 62 |
| Tensile Modulus |
|
|
|
|
-- 4
|
|
psi
|
ASTM D638 |
|
--
|
|
psi
|
ISO 527-2/1 |
| Tensile Strength |
|
|
|
|
Yield 5
|
|
psi
|
ASTM D638 |
|
Yield
|
|
psi
|
ISO 527-2/50 |
|
Break 5
|
|
psi
|
ASTM D638 |
|
Break
|
|
psi
|
ISO 527-2/50 |
| Tensile Elongation |
|
|
|
|
Yield 5
|
|
%
|
ASTM D638 |
|
Yield
|
|
%
|
ISO 527-2/50 |
|
Break 5
|
|
%
|
ASTM D638 |
|
Break
|
|
%
|
ISO 527-2/50 |
| Flexural Modulus |
|
|
|
|
1.97 in Span 6
|
|
psi
|
ASTM D790 |
|
-- 7
|
|
psi
|
ISO 178 |
| Flexural Strength |
|
|
|
|
-- 7, 8
|
|
psi
|
ISO 178 |
|
Yield, 1.97 in Span 6
|
|
psi
|
ASTM D790 |
|
Break, 1.97 in Span 6
|
|
psi
|
ASTM D790 |
| Charpy Notched Impact Strength 9 (73°F) |
|
ft·lb/in²
|
ISO 179/1eA |
| Notched Izod Impact |
|
|
|
|
-22°F
|
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
|
ft·lb/in
|
ASTM D256 |
|
-22°F 10
|
|
ft·lb/in²
|
ISO 180/1A |
|
73°F 10
|
|
ft·lb/in²
|
ISO 180/1A |
| Unnotched Izod Impact (73°F) |
|
|
ASTM D4812 |
| Instrumented Dart Impact (73°F, Total Energy) |
|
in·lb
|
ASTM D3763 |
| Gardner Impact |
|
|
ASTM D3029 |
|
73°F
|
|
in·lb
|
|
|
73°F 11
|
|
in·lb
|
|
| Rockwell Hardness (R-Scale) |
|
|
ASTM D785 |
| Deflection Temperature Under Load |
|
|
|
|
66 psi, Unannealed, 0.126 in
|
|
°F
|
ASTM D648 |
|
66 psi, Unannealed, 0.252 in
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed, 0.126 in
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed, 0.252 in
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed, 2.52 in Span 12
|
|
°F
|
ISO 75-2/Af |
| Vicat Softening Temperature |
|
|
|
|
--
|
|
°F
|
ASTM D1525 13 |
|
--
|
|
°F
|
ISO 306/B50 |
|
--
|
|
°F
|
ISO 306/B120 |
| CLTE |
|
|
|
|
Flow: -40 to 104°F
|
|
in/in/°F
|
ASTM E831 |
|
Flow: 140 to 280°F
|
|
in/in/°F
|
ASTM E831 |
|
Flow: -40 to 104°F
|
|
in/in/°F
|
ISO 11359-2 |
|
Transverse: -40 to 104°F
|
|
in/in/°F
|
ASTM E831, ISO 11359-2 |
| Volume Resistivity |
|
ohm·cm
|
ASTM D257 |
| Dielectric Strength |
|
|
ASTM D149 |
|
0.0630 in, in Oil
|
|
V/mil
|
|
|
0.126 in, in Air
|
|
V/mil
|
|
|
0.126 in, in Oil
|
|
V/mil
|
|
| Dielectric Constant |
|
|
ASTM D150 |
|
100 Hz
|
|
|
|
|
1 MHz
|
|
|
|
| Dissipation Factor |
|
|
ASTM D150 |
|
100 Hz
|
|
|
|
|
1 MHz
|
|
|
|
| Arc Resistance (PLC) 14 |
|
|
ASTM D495 |
| Flame Rating - UL |
|
|
UL 94 |
|
0.0177 in
|
|
|
|
|
0.0248 in
|
|
|
|
|
0.118 in
|
|
|
|
| Oxygen Index |
|
%
|
ASTM D2863 |
| RTI Str |
|
°F
|
UL 746 |
| RTI Imp |
|
°F
|
UL 746 |
| RTI Elec |
|
°F
|
UL 746 |
| Comparative Tracking Index (CTI) (PLC) |
|
|
UL 746 |
| High Voltage Arc Tracking Rate (HVTR) (PLC) |
|
|
UL 746 |
| Hot-wire Ignition (HWI) (PLC) |
|
|
UL 746 |
| High Amp Arc Ignition (HAI) (PLC) |
|
|
UL 746 |
| Outdoor Suitability |
|
|
UL 746C |
|
This supplier and product may also be known by these terms: GE Plastics, LNP Engineering Plastics, GE Polymerland
Product names can be difficult to match. You may have searched any one of these terms to find this product: VALOX* 357 Resin, VALOX 357 Resin, VALOX* , VALOX, VALOX357Resin, 357 Resin, 357Resin, Polybutylene Terephthalate, PBT, Polyester, SABIC IP, PolybutyleneTerephthalate, Resin357
|
|
This plastic material has approval for 1 automotive specifications from the following agencies (the number in parentheses shows the number of specifications for that agency): FORD (1).
|