Density
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (235°C/2.16 kg)
|
|
g/10 min
|
ISO 1133 |
|
Molding Shrinkage
|
|
|
ISO 294-4 |
|
Across Flow
|
|
%
|
|
|
Flow
|
|
%
|
|
|
Water Absorption (73°F, 24 hr)
|
|
%
|
ISO 62 |
|
Tensile Stress (Yield)
|
|
psi
|
ISO 527-2 |
|
Tensile Strain
|
|
|
ISO 527-2 |
|
Yield
|
|
%
|
|
|
Break
|
|
%
|
|
|
Flexural Modulus
|
|
psi
|
ISO 178 |
|
Flexural Strength
|
|
psi
|
ISO 178 |
|
Charpy Notched Impact Strength
|
|
|
ISO 179/1eA |
|
-40°F, Complete Break
|
|
ft·lb/in²
|
|
|
73°F, Partial Break
|
|
ft·lb/in²
|
|
|
Rockwell Hardness (R-Scale)
|
|
|
ISO 2039-2 |
|
Shore Hardness (Shore D)
|
|
|
ISO 868 |
|
Heat Deflection Temperature
|
|
|
|
|
66 psi, Unannealed
|
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
|
°F
|
ISO 75-2/A |
|
Melting Temperature (DSC)
|
|
°F
|
ISO 3146 |
|
CLTE - Flow
|
|
in/in/°F
|
ISO 11359-2 |
|
Volume Resistivity
|
|
ohm·cm
|
IEC 60093 |
|
The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.
Tensile Strain at Break, ISO 527: >200%
Abrasion Loss, ISO 9352, CS-17, 1000 rev.: 8 mg
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: UBESTA 3030 JLX1, UBESTA , UBESTA3030JLX1, 3030 JLX 1, 3030 JLX1, 3030JLX, JLX1, 3030JLX1, Polyamide 12, Nylon 12, Polyamide, Nylon, pa12, UBE Engineering Plastics, Polyamide12, Nylon12, JLX3030
|
|
Generic Name may also be described by the following terms: PA12.
|
|
Features may also be described by the following terms: Heat Stabilized, Heat-ageing Stabilized, Heat Ageing Stabilized, Heat-aging Stabilized, Heat Aging Stabilized, Good Processability, Easy Processing.
|
|
Uses may also be described by the following terms: Tubing, Tube.
|
|
This plastic material has 1 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): DIN (1).
|