NORYL GTX GTX6203 Resin SABIC IP Asia Polyphenylene Ether + PS + Nylon (Talc Filler, 20%)

Product Description

NORYL GTX6203 is a 20% talc filled material with superior dimensional stability, excellent processability and surface appearance.

General

Material Status

Commercial: Active

Availability

Asia Pacific

Filler / Reinforcement

Talc Filler, 20% Filler by Weight

Features

Good Dimensional Stability

Good Processability

Good Surface Finish

Processing Method

Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity
--			ASTM D792
--		g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (280°C/5.0 kg)		g/10 min	ASTM D1238
Melt Volume-Flow Rate (MVR) (280°C/5.0 kg)		in³/10min	ISO 1133
Molding Shrinkage			Internal Method
Flow: 0.126 in		in/in
Across Flow: 0.126 in		in/in
Water Absorption			ISO 62
Saturation, 73°F		%
Equilibrium, 73°F, 50% RH		%
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
--²		psi	ASTM D638
--		psi	ISO 527-2/1
Tensile Strength
Yield³		psi	ASTM D638
Yield		psi	ISO 527-2/50
Break³		psi	ASTM D638
Break		psi	ISO 527-2/50
Tensile Elongation
Yield³		%	ASTM D638
Yield		%	ISO 527-2/5
Break³		%	ASTM D638
Break		%	ISO 527-2/5, ISO 527-2/50
Flexural Modulus
1.97 in Span⁴		psi	ASTM D790
--⁵		psi	ISO 178
Flexural Strength
--^5, 6		psi	ISO 178
Yield, 1.97 in Span⁴		psi	ASTM D790
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength⁷ (73°F)		ft·lb/in²	ISO 179/1eA
Notched Izod Impact
-22°F		ft·lb/in	ASTM D256
73°F		ft·lb/in	ASTM D256
-22°F⁸		ft·lb/in²	ISO 180/1A
73°F⁸		ft·lb/in²	ISO 180/1A
Unnotched Izod Impact Strength⁸ (73°F)		ft·lb/in²	ISO 180/1U
Instrumented Dart Impact (73°F, Total Energy)		in·lb	ASTM D3763
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
66 psi, Unannealed, 0.126 in		°F	ASTM D648
66 psi, Unannealed, 3.94 in Span⁹		°F	ISO 75-2/Be
Vicat Softening Temperature
--		°F	ASTM D1525¹⁰
--		°F	ISO 306/B50, ISO 306/B120
Ball Pressure Test (257°F)			IEC 60695-10-2
CLTE
Flow: -40 to 104°F		in/in/°F	ASTM E831
Flow: 73 to 176°F		in/in/°F	ISO 11359-2
Transverse: -40 to 104°F		in/in/°F	ASTM E831
Transverse: 73 to 176°F		in/in/°F	ISO 11359-2
Thermal Conductivity		Btu·in/hr/ft²/°F	ISO 8302
Related Terminology
This supplier and product may also be known by these terms: GE Plastics, LNP Engineering Plastics Product names can be difficult to match. You may have searched any one of these terms to find this product: NORYL GTX* GTX6203 Resin, NORYL GTX GTX6203 Resin, NORYL GTX* , NORYL GTX, NORYLGTXGTX6203Resin, NORYLGTX, GTX 6203 Resin, GTX6203 Resin, GTX6203, 6203Resin, GTX6203Resin, Polyphenylene Ether + PS + Nylon, Polyphenylene Ether PS Nylon, Polyphenylene Ether : PS : Nylon, Polyphenylene Ether / PS / Nylon, Polyphenylene Ether - PS - Nylon, Polyphenylene Ether _ PS _ Nylon, Polyphenylene Ether PS Nylon, PPE+PS+Nylon, PPEPSNylon, PPE:PS:Nylon, PPE/PS/Nylon, PPE-PS-Nylon, PPE_PS_Nylon, PPE PS Nylon, Polyphenylene Ether, PPE, SABIC IP Asia, PolyphenyleneEtherPSNylon, PolyphenyleneEther, PolyphenyleneEther_PS_Nylon, 6203GTX
Features
Features may also be described by the following terms: Good Surface Finish, Good Processability, Easy Processing, Good Dimensional Stability, Dimensionally Stable.

Injection	Nominal Value	Unit
Drying Temperature		°F
Drying Time		hr
Suggested Max Moisture		%
Hopper Temperature		°F
Rear Temperature		°F
Middle Temperature		°F
Front Temperature		°F
Nozzle Temperature		°F
Processing (Melt) Temp		°F
Mold Temperature		°F
Injection Notes
Minimum Moisture Content: 0.02 %

Notes

¹Typical properties: these are not to be construed as specifications.

²0.20 in/min

³Type I, 0.20 in/min

⁴0.051 in/min

⁵0.079 in/min

⁶Yield

⁷80*10*4 sp=62mm

⁸80*10*4

⁹120*10*4 mm

¹⁰Rate B (120°C/h), Loading 2 (50 N)

NORYL GTX* GTX6203 Resin

Polyphenylene Ether + PS + Nylon

Talc Filler, 20%

Supplied by SABIC Innovative Plastics Asia Pacific