Plaslube® J-1/30/TF/13/SI/2 Techmer Lehvoss Polyamide 66 (Glass Fiber Reinforcement, 30%)

General

Material Status

Commercial: Active

Availability

Africa & Middle East

Asia Pacific

Europe

North America

South America

Filler / Reinforcement

Glass Fiber Reinforcement, 30% Filler by Weight

Additive

PTFE Lubricant (13%)

Silicone Lubricant (2%)

Features

Lubricated

RoHS Compliance

Forms

Pellets

Processing Method

Injection Molding

Physical	Dry	Conditioned	Unit	Test Method
Specific Gravity
--		--		ASTM D792
--		--	lb/in³	ISO 1183²
Molding Shrinkage - Flow (0.125 in)		--	in/in	ASTM D955
Water Absorption
24 hr		--	%	ASTM D570
Saturation		--	%	ISO 62²
Equilibrium		--	%	ISO 62²
Mechanical	Dry	Conditioned	Unit	Test Method
Tensile modulus			psi	ISO 527-2²
Tensile Stress
Break			psi	ISO 527-2²
73°F		--	psi	ASTM D638
Tensile Elongation
Break, 73°F		--	%	ASTM D638
Break			%	ISO 527-2²
Flexural Modulus (73°F)		--	psi	ASTM D790
Flexural Strength (73°F)		--	psi	ASTM D790
Compressive Strength		--	psi	ASTM D695
Impact	Dry	Conditioned	Unit	Test Method
Charpy notched impact strength				ISO 179/1eA²
-22°F		--	ft·lb/in²
73°F			ft·lb/in²
Notched Izod Impact (73°F, 0.125 in)		--	ft·lb/in	ASTM D256
Hardness	Dry	Conditioned	Unit	Test Method
Rockwell Hardness (R-Scale)		--		ASTM D785
Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
66 psi		--	°F	ISO 75-2²
264 psi, Unannealed		--	°F	ASTM D648
264 psi		--	°F	ISO 75-2²
Melting Temperature³		--	°F	ISO 11357-3²
CLTE - Flow		--	in/in/°F	ASTM D696
Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating - UL (0.0625 in)		--		UL 94
Burning Behav. at 1.6mm nom. thickn. (0.06 in, UL)		--		ISO 1210²
Additional Information
Dry	Compressive Strength, ASTM D695, 73°F: 24000 psi
Related Terminology
Dry	Product names can be difficult to match. You may have searched any one of these terms to find this product: Plaslube® J-1/30/TF/13/SI/2, Plaslube J130TF13SI2, Plaslube® , Plaslube, PlaslubeJ130TF13SI2, J 1 30 TF 13 SI 2, J-1/30/TF/13/SI/2, J130TF13SI2, J-1:30:TF:13:SI:2, J-1+30+TF+13+SI+2, J-1-30-TF-13-SI-2, J-1_30_TF_13_SI_2, J-1 30 TF 13 SI 2, J:1/30/TF/13/SI/2, J/1/30/TF/13/SI/2, J+1/30/TF/13/SI/2, J_1/30/TF/13/SI/2, J 1/30/TF/13/SI/2, J1, 130, 30TF, TF13, 13SI, SI2, J1_30_TF_13_SI_2, J1 30 TF 13 SI 2, J_130TF13SI2, J 130TF13SI2, Polyamide 66, Nylon 66, Polyamide, Nylon, pa66, Techmer Lehvoss, Polyamide66, Nylon66, 1J
Generic Name
Dry	Generic Name may also be described by the following terms: PA66.
Conditioned	Product names can be difficult to match. You may have searched any one of these terms to find this product: Plaslube® J-1/30/TF/13/SI/2, Plaslube J130TF13SI2, Plaslube® , Plaslube, PlaslubeJ130TF13SI2, J 1 30 TF 13 SI 2, J-1/30/TF/13/SI/2, J130TF13SI2, J-1:30:TF:13:SI:2, J-1+30+TF+13+SI+2, J-1-30-TF-13-SI-2, J-1_30_TF_13_SI_2, J-1 30 TF 13 SI 2, J:1/30/TF/13/SI/2, J/1/30/TF/13/SI/2, J+1/30/TF/13/SI/2, J_1/30/TF/13/SI/2, J 1/30/TF/13/SI/2, J1, 130, 30TF, TF13, 13SI, SI2, J1_30_TF_13_SI_2, J1 30 TF 13 SI 2, J_130TF13SI2, J 130TF13SI2, Polyamide 66, Nylon 66, Polyamide, Nylon, pa66, Techmer Lehvoss, Polyamide66, Nylon66, 1J Generic Name may also be described by the following terms: PA66.

Injection	Dry	Unit
Drying Temperature		°F
Drying Time		hr
Suggested Max Moisture		%
Rear Temperature		°F
Middle Temperature		°F
Front Temperature		°F
Nozzle Temperature		°F
Processing (Melt) Temp		°F
Mold Temperature		°F
Injection Rate
Back Pressure		psi
Injection Notes
Screw Speed: Medium Recommendations for Molding and Tool Conditions: Well vented Moisture Content, as received: Product is packaged at 0.2% or less. Recomended Max Moisture: 0.12% down to 0.08%

Notes

¹Typical properties: these are not to be construed as specifications.

²Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.

³18 °F/min

Plaslube® J-1/30/TF/13/SI/2

Polyamide 66

Glass Fiber Reinforcement, 30%

Supplied by Techmer Lehvoss Compounds