Specific Gravity
|
|
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
|
|
g/10 min
|
ASTM D1238 |
|
Molding Shrinkage
|
|
|
ASTM D955 |
|
Flow: 0.118 in
|
|
in/in
|
|
|
Across Flow: 0.118 in
|
|
in/in
|
|
|
Water Absorption (73°F, 24 hr)
|
|
%
|
ASTM D570 |
|
Tensile Strength
|
|
psi
|
ASTM D638 |
|
Tensile Elongation (Break)
|
|
%
|
ASTM D638 |
|
Flexural Modulus
|
|
psi
|
ASTM D790 |
|
Flexural Strength
|
|
psi
|
ASTM D790 |
|
Shear Strength
|
|
psi
|
ASTM D732 |
|
Coefficient of Friction
|
|
|
ASTM D1894 |
|
vs. Itself - Dynamic
|
|
|
|
|
vs. Metal - Dynamic
|
|
|
|
|
Notched Izod Impact
|
|
ft·lb/in
|
ASTM D256 |
|
Unnotched Izod Impact
|
|
ft·lb/in
|
ASTM D256 |
|
Tensile Impact Strength
|
|
ft·lb/in²
|
ASTM D1822 |
|
Rockwell Hardness
|
|
|
ASTM D785 |
|
M-Scale
|
|
|
|
|
R-Scale
|
|
|
|
|
Deflection Temperature Under Load
|
|
|
ASTM D648 |
|
66 psi, Unannealed
|
|
°F
|
|
|
264 psi, Unannealed
|
|
°F
|
|
|
Melting Temperature
|
|
°F
|
DSC |
|
CLTE - Flow
|
|
in/in/°F
|
ASTM D696 |
|
Volume Resistivity
|
|
ohm·cm
|
ASTM D257 |
|
Dielectric Strength
|
|
V/mil
|
ASTM D149 |
|
Dielectric Constant
|
|
|
ASTM D150 |
|
50 Hz
|
|
|
|
|
1 MHz
|
|
|
|
|
Dissipation Factor
|
|
|
ASTM D150 |
|
50 Hz
|
|
|
|
|
1 MHz
|
|
|
|
|
Arc Resistance
|
|
sec
|
ASTM D495 |
|
Flame Rating - UL
|
|
|
UL 94 |
|
Comparative Tracking Index (CTI)
|
|
V
|
UL 746 |
|
The value listed as Comparative Track Index, UL 746, was tested in accordance with IEC test methods.
The values listed as Mold Shrinkage, ASTM D955, were tested in accordance with Toray test methods.
Flammability, UL-94: HB Equivalent
Comparative Track Index, IEC: >600 V
Arc Resistance, ASTM D495: >200 sec
Mold Shrinkage, Toray test method, Flow, 80 mm x 80 mm x 3 mm: 1.8%
Mold Shrinkage, Toray test method, Transverse, 80 mm x 80 mm x 3 mm: 1.9%
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Amilus™ S731, Amilus S731, Amilus™ , Amilus, AmilusS731, S 731, S731, Acetal Copolymer, Acetal Copolymer, Acetal (POM) Copolymer, Acetal POM Copolymer, Acetal, pom, Toray, AcetalPOMCopolymer, 731S
|
|
Features may also be described by the following terms: High Flow, High Melt, High MFI, Good Stability, Low Odor, Low Outgassing, Good Creep Resistance, Creep Resistant, Excellent Elastic Recovery, High Elastic Recovery, Good Electrical Properties, Good Dimensional Stability, Dimensionally Stable, Low Water Absorption, Low Moisture Absorption, Water Resistant, Moisure Resistant, Good Chemical Resistance, Chemical Resistant.
|