Fortron® 0205

Polyphenylene Sulfide

Supplied by Ticona

The technical datasheet with complete property values for Fortron® 0205 is available to members of the Prospector Plastics Database.
Register to view full datasheet.
Register to View Full Datasheet
Product Description
0205 is an easy flowing unfilled grade. It demonstrates excellent chemical resistance and thermal stability. Intended for compounding with various fillers. Available standard in pellet (0205P4) and powder (0205B4) form.
General  
Material Status 
  • Commercial: Active
Availability 
  • Africa & Middle East
  • Europe
  • Latin America
  • North America
  • South America
Features 
  • Flame Retardant
  • Good Chemical Resistance
  • Good Flow
  • Good Thermal Stability
  • Halogen Free
Uses 
  • Compounding
RoHS Compliance 
Forms 
  • Pellets
  • Powder
  
Processing Method 
  • Injection Molding
Physical
Nominal Value
Unit
Test Method
Specific Gravity
      
--
 
 ASTM D792
--
g/cm³
 ISO 1183
Specific Volume
in³/lb
 ASTM D792
Molding Shrinkage
      
Flow
in/in
 ASTM D955
Across Flow
in/in
 ASTM D955
Across Flow
%
 ISO 294-4
Flow
%
 ISO 294-4
Water Absorption
      
73°F, 24 hr
%
 ASTM D570
Saturation, 73°F
%
 ISO 62
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
psi
 ISO 527-2/1A/1
Tensile Strength
      
Break, 73°F
psi
 ASTM D638
Break
psi
 ISO 527-2/1A/5
Tensile Strain (Break)
%
 ISO 527-2/1A/5
Flexural Modulus
      
73°F
psi
 ASTM D790
73°F
psi
 ISO 178
Flexural Strength
      
73°F
psi
 ASTM D790
-- 2
psi
 ISO 178
Impact
Nominal Value
Unit
Test Method
Notched Izod Impact
      
73°F
ft·lb/in
 ASTM D256
73°F
ft·lb/in²
 ISO 180/1A
Unnotched Izod Impact
      
73°F
ft·lb/in
 ASTM D256
73°F
ft·lb/in²
 ISO 180/1U
Hardness
Nominal Value
Unit
Test Method
Rockwell Hardness
      
M-Scale
 
 ASTM D785
M-Scale
 
 ISO 2039-2
Thermal
Nominal Value
Unit
Test Method
Deflection Temperature Under Load
      
66 psi, Unannealed
°F
 ASTM D648
264 psi, Unannealed
°F
 ASTM D648
264 psi, Unannealed
°F
 ISO 75-2/A
1160 psi, Unannealed
°F
 ISO 75-2/C
Glass Transition Temperature
°F
 ISO 11357-2
Melting Temperature 3
°F
 ISO 11357-3
CLTE
     ISO 11359-2
Flow
in/in/°F
  
Transverse
in/in/°F
  
Electrical
Nominal Value
Unit
Test Method
Volume Resistivity
      
--
ohm·cm
 ASTM D257
--
ohm·cm
 IEC 60093
Dielectric Constant
     ASTM D150
1 kHz
 
  
1 MHz
 
  
Dissipation Factor
     ASTM D150
1 kHz
 
  
1 MHz
 
  
Arc Resistance
sec
 ASTM D495
Comparative Tracking Index
V
 IEC 60112
Electric Strength
V/mil
 IEC 60243-1
Fill Analysis
Nominal Value
Unit
Test Method
Melt Specific Heat
Btu/lb/°F
 ASTM C351
Additional Information
Nominal Value
Unit
Test Method
Effects of Acids
 
 ASTM D543
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Fortron® 0205, Fortron 0205, Fortron® , Fortron, Fortron0205, 0205, Polyphenylene Sulfide, PPS, Ticona, PolyphenyleneSulfide
Features
Features may also be described by the following terms: Good Thermal Stability, Good Chemical Resistance, Chemical Resistant, Good Flow, Zero Halogen Content, Halogen Free.
Uses
Uses may also be described by the following terms: Compounding, Compounds.
Injection
Nominal Value
Unit
 
Processing (Melt) Temp
°F
  
Mold Temperature
°F
  
Injection Notes
On injection molding machines with 15-25 D long three-section screws, are usual in the trade, the unreinforced FORTRON is processable. A shut-off nozzle is recommended.

A medium injection rate is normally preferred. All mold cavities must be effectively vented.
Notes
1Typical properties: these are not to be construed as specifications.
2at Break
310°C/min
 
IDES
Copyright © 2012 IDES
The information presented on this datasheet was acquired by IDES from the producer of the material. IDES makes substantial efforts to assure the accuracy of this data. However, IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.