Impact Flexural Test, ISO 179/2C, Notched: 2 kJ/m²
Impact Flexural Test, ISO 179/2D, Unnotched: 22 kJ/m²
Vicat Softening Temp, DIN 53460, 50°C/hr ; 1 kg: 118°C
Vicat Softening Temp, DIN 53460, 50°C/hr ; 5 kg: 106°C
Vicat Softening Temp, DIN 53460, 120°C/hr ; 1 kg: 115°C
Vicat Softening Temp, DIN 53460, 120°C/hr ; 5 kg: 109°C
DTUL @ 1.80 MPa, DIN 53461, Unannealed: 87°C
DTUL @ 1.80 MPa, DIN 53461, Annealed: 106°C
Impact Flexural Test, DIN 53453, Notched: 2 kJ/m²
Impact Flexural Test, DIN 53453, Unnotched: 22 kJ/m²
Tensile Strength @ Yield, DIN 53455, 50 mm/min: 72 MPa
Tensile Strength @ Break, DIN 53455, 50 mm/min: 73 MPa
Tensile Elongation, DIN 53455, 50 mm/min: 15%
Flexural Strength, DIN 53452, 2 mm/min: 101 MPa
Flexural Modulus, DIN 53452, 2 mm/min: 2.8 GPa
Mass Density, DIN 53479-A, 23°C: 1.19 g/cm³
|
|
This supplier and product may also be known by these terms: ChiMei
Product names can be difficult to match. You may have searched any one of these terms to find this product: ACRYREX® CM-206, ACRYREX CM206, ACRYREX® , ACRYREX, ACRYREXCM206, CM, CM-206, CM206, CM:206, CM/206, CM+206, CM_206, CM 206, Acrylic, Acrylic, Polymethyl Methacrylate, Acrylic Polymethyl Methacrylate, Acrylic (PMMA), Acrylic PMMA, pmma, Chi Mei, AcrylicPolymethylMethacrylate, AcrylicPMMA, 206CM
|